Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X
DEVELOPMENT OF POLYURETHANE/CLAY NANOCOMPOSITES BASED ON
PALM OIL POLYOL
Ummi Habibah1*.
Adriana1.
S Sariadi1.
Muhammad2.
Halim Zaini1.
Sabila Yasara SA1.
Fachraniah1 Jurusan Teknik Kimia.
Politeknik Negeri Lhokseumawe.
Jl.
Medan - Banda Aceh No.
Km.
RW.
Buketrata.
Mesjid Punteut.
Blang Mangat.
Kota Lhokseumawe.
Aceh 24301 Jurusan Teknik Elektro.
Universitas Malikussaleh.
Jl.
Batam.
Blang Pulo.
Kec.
Muara Satu.
Kota Lhokseumawe.
Aceh 24355 *E-mail:ummihabibah@pnl.
ABSTRACT
Polyurethanes (PUR.
are highly adaptable polymeric substances with a variety of physical and chemical attributes.
High abrasion resistance, tear strength, shock absorption, flexibility, and elasticity are just a few of the desirable qualities of PURs.
Despite their generally low thermal stability, this can be enhanced by utilizing clay that has been treated.
From renewable resources, polyurethane/clay nanocomposites have been created.
By combining oleic acid from palm oil with glycerol, a polyol for the manufacture of polyurethane by reaction with an isocyanate was created.
As a catalyst and emulsifier, dodecylbenzene sulfonic acid (DBSA) was employed.
Octadodecylamine (ODA-mon.
and cetyltrimethyl ammonium bromide (CTAB-mon.
were used to treat the unaltered clay .
unipiaF).
The d-spacing in CTAB-mont and ODA-mont were bigger than that of the pure-mont .
142 n.
571 nm and 1.
798 nm, respectively.
A pre-polymer technique was used to create polyurethane/clay nanocomposites, and the micro-domain structures of segmented PU.
CTAB-montPU 1, 3, and 5 wt%, and ODA-mont-PU 1, 3, and 5 wt% were determined by FTIR spectra.
X-ray diffraction (X-RD) was used to evaluate the nanocomposites' morphology, and the results revealed that all of the intercalated type's nanocomposites were created as a result of this effort.
When the surfaces of the materials were examined using transmission electron microscopy (TEM) observation and scanning electron microscopy (SEM), these were further confirmed.
Thermogravimetric analysis (TGA) was used to examine thermal stability.
Pure PU begins to degrade around 200AC, which is lower than the degrading rates of CTAB-mont PU and ODA-mont PU, which occur at roughly 318AC and 330AC, respectively.
Both pure polyurethane (PU) and PU/clay nanocomposites have their mechanical properties, including dynamic mechanical properties, tested.
With only a 5 weight percent addition of the montmorillonite CTAB-mont PU or ODA-mont PU, respectively, the tensile strength of the nanocomposites increased by more than 214% and 267%, respectively, demonstrating the impressively positive impact of the modified organoclay on the strength and elongation at break of the nanocomposites.
Keywords: Clay,Palm Oil.
Polyurethane petrochemical products.
Petrochemicals are based on finite resources of which, optimistic calculations assumed an availability of mineral oil for approximately 50 years.
Sooner or later new alternative resources should be prepared or explored.
Many years ago, price of mineral oil are as low as compared to the bio-based materials.
That is why research on the use of renewable resources is not of the public interests.
But in the event of oil crisis and unpredictable price, we must pay more attention on finding an alternative from fossil which is finite to renewable bio-based resources.
Amongst
INTRODUCTION
Manufacturing of high molecular weight polyurethane elastomers (PU.
needs at least two groups as reactants: compounds with isocyanate groups .
NHCO-O-) and compounds with hydroxyl groups .
olyethers, polyester, et.
PUs are very important products related to their high hardness for given modulus, high abrasion mechanical and elastic properties [Petrovic and Ferguson, 1.
Currently, majority of the hydroxyl groups or most called polyols used for making Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X advantages of bio-based materials are their non-toxicity, noncarcinogenicity and renewable resources which are very close to green environmental, because almost all of them are coming from agricultural products [Warwel et al.
, 2.
Since it was first synthesized in 1853, many studies on the production of polyol from agricultural products were carried out [Lu et al.
, 2005.
Latere DwanAoisa et al, 2004.
Silva Arayjo et , 2004.
Uyama et al.
, 2.
In the present studies, we are more interested in exploring about the potential of using palm oil as raw materials in polyol production since, almost 80% of worldwide production renewable resources are based on plants oils, i.
soybean oil, palm oil, sunflower oil, olive oil, tung seed oils etc.
Despite the versatility of PUs, they also have some limitations notably having lower thermal stability compared to other polymers.
In order to solve this problem, we can employ modified clay montmorillonite (MMT) in the formulations for certain applications.
For example, by adding minimum amount (<10 %) of MMT in the formulation, the mechanical and thermal properties of the composites could be enhanced significantly [Wang et al.
, 2.
great profits for the community given the fourier transform infrared spectra (FTIR) to determine micro-domain structures.
The morphology of the nanocomposites was characterized by X-ray diffraction (X-RD) and flame retardant was investigated with thermogravimetric analysis (TGA).
The mechanical properties are analyzed by using instron and dynamic mechanical analysis (DMA).
Materials used in this study were:
Kunipia F .
upplied by Kunimine Ind.
Co.
it is a Na type montmorillonite, with a cation exchange capacity of 119 meq/100 .
, 4,4-diphenylmethane diisocyanate (MDI.
Merc.
, polyol based on palm oil .
atent application no.
PI20043190, used materials : palm oil based oleic acid .
4-dodecylbenzenesulfonic acid, extruded 3A molecular sieve.
Aldric.
, 1.
4-butanediol .
,4-BDO.
Fluk.
, cetyltrimethyl ammonium bromide (CTAB.
Fluk.
, octadodecylamine (ODA.
Merc.
and dimethylformamide (DMF, 99%.
Fishe.
as a solvent.
Other inorganic and organic materials that were used in this study were obtained from commercially available source, such as : Natrium Chlorid (NaCl.
Merc.
Ethyl Alcohol (C2H5OH, 95%.
Syster.
and Dioxane (Mallinckrod.
The experiments were carried out in a 250 ml three-necked flask fitted with a mechanical stirrer and a cooling system.
The operation conditions were as follows: oleic acid, glycerol, dodecylbenzene sulfonic acid (DBSA), and an extruded 3A molecular After filtration to remove the molecular sieves, the reaction mixture was washed with a solution of NaCl to remove excess glycerol.
Polyol based on palm oil was prepared by the reaction of oleic acid and glycerol.
Since the two reactants are not miscible, need to added additives to favor contact between them.
Surfactant such as CTAB or DBSA will be producing a homogeneous reaction.
In this case.
DBSA choose as emulsifier in this system.
Because DBSA can work in dual action, as emulsifier and as catalyst.
In the presence of DBSA, all esters of glycerol are formed.
Although the conversion of oleic acid was elevated, little RESEARCH METHODS This chapter details the preparation and characterization of polyol based on palm oil, synthesis of polyurethane based on palm oil, preparation and characterization of organophilic clay and lastly synthesis and Polyurethane/clay nanocomposites based on palm oil polyol.
The properties of polyol were determined using fourier transform infrared spectra (FTIR) and gel permeation chromatography apparatus (GPC).
Organophilic clay was analysis using the X-ray diffraction (X-RD) as an effective method for examining the crystal structure of pristine clay and clay Finally.
Polyurethane/clay nanocomposites were monitored by a prepolymer method and were evaluated by Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X glycerol monooleate was formed [Eychenne and Mouloungui, 1.
The polyurethane-terminated prepolymer was prepared by reacting MDI and polyol at a specified NCO/OH equivalent ratio by using the following procedure.
Polyol .
in DMF was placed in a 0.
5L glass reaction kettle, which was equipped with a mechanical stirrer, thermometer, heating mantle and a gas inlet and outlet for continuous flow of nitrogen.
When the temperature of the isocyanate reached 70oC.
MDI .
was added in several portions to the reactor under constant The reaction temperature was maintained at 70oC to 80oC and periodic samples were withdrawn to determine the isocyanate content.
After the theoretical NCO% value was reached .
sing FTIR grap.
, the reaction was stopped by cooling and the prepolymer stored in a sealed glass bottle under nitrogen.
In the second step, the prepolymer was heated at 90-100oC and a specified amount of the prepolymer was weighed into a 250 ml plastic cup.
The chain extender .
,4 -BDO) .
08 gram.
, which was preheated at 100oC, was added to the prepolymer under vigorous mixing.
The TPU films were formed by casting the solution in a mold and remove the solvent under pressure at 70oC.
The flow diagram for preparation of polyurethane is shown in Figure 1.
500 ml beaker.
These solutions were heated at 80oC for 1 h.
Twenty .
grams of Kunipia-F and 500 ml of distilled water were dispersed in a 1000 ml beaker.
The dispersion of Kunipia-F was added to the solution of ammonium salt of CTAB, and this mixture was stirred vigorously for 1 h [Yano et al.
, 1.
The treated Kunipia-F was repeatedly washed by distilled water.
The filtrate was titrated with 0.
1 N AgNO3 until there is no chloride or bromide present.
The filter cake was then placed for drying in an oven at 60oC.
The organophilic KunipiaF was ground and particles of size less than 100 m were collected by using sieve tray for preparation of nanocomposite.
The product was termed CTAB-mont.
For the preparation of octadecylamine (ODAmon.
, a similar procedure as for the preparation of CTAB-mont was adopted.
The flow diagram for preparation of organoclay is shown in Figure 2.
CTAB
KUNIPIA -F
600 ml H2O Stirring 250 ml H2O Heating 80oC Stirring Filtrate and washed with hot distilled Chloride Test pre-polymer polymerization 6 grams 4,4'-diphenylmethane diisocyanate (MDI) Yes Washed with hot distilled water untill there is no chloride or bromide Dryed in oven 60oC 12 grams Poly .
etramethylene adipat.
glycol (PTMEG) dissolved in DMF solvent Dryed in oven 60oC Heated at 90oC Stirrer for 2.
5 hrs Figure 2 Synthesis of organophilic clays 08 grams 1,4 - Butanediol Heated at 90oC Rapid stirrer for 10 min Polyurethane/clay nanocomposites were prepared by melt blending [Figure .
In this study, the amounts of organoclay used in the PU/clay nanocomposites were 1, 3, 5 wt% of polyurethane, respectively.
The total volume in each blending was 40 gr.
Mixings were carried out using a laboratory internal mixer (Haake Polydriv.
at temperature setting of 80oC and a rotor speed of 50 rpm.
The Next steps more stirring at room temperatur for 3 hrs Polyurethane film were formed by casting the solution in a mold and then removing the solvent at 70oC Figure 1 Synthesis of Polyurethane An amount of 0.
05 mol .
2 gram.
of cetyl trimetyl ammonium bromide (CTAB) and 250 mL of distilled water were placed in a Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X compounds were then compressed using HSINCHU moulded into 1 mm thickness sheets under a pressure of 98 x 105 Pa at 100oC to produce sample sheets [Figure Similar procedures were done for ODA-mont.
The physical appearance of clay nanocomposite in inserted in Figure 3 Manufacturing polyurethane elastomers (PUE.
needs at least two groups as reactants: compounds with isocyanate groups and compounds hydroxyl groups .
In this study, we are using palm oil as raw materials for production polyol.
Oleic acid and glycerol was synthesized by direct esterification in the absence of Since the two reactants are not miscible, additives was employed to favor contact between them.
The employed additives can produce a homogeneous reaction system also and dodecylbenzene sulfonic acid (DBSA) selected as it has both emulsifying and catalytic activity [Eychenne and Mouloungui, 1.
The preparation of polyol from palm oil based oleic acid and glycerol was monitored by FTIR spectroscopy.
Some notable features of the IR spectra include 3384.
O-H), 2926.
C-H saturatio.
, 362 .
C=O), 1462.
CH=CH) and 186 and 1039.
892 cm-1 .
C-O-C) are presented in Figure 3.
1 The micro domain structures of the segmented PU were analyzed by FTIR as shown in Figure 4.
These steps a process synthesis of polyurethane based on palm oil polyol.
The collect data start from 0 hour which the peak of isocyanate still in full and finished of synthesis if the peak of isocyanate were disappearances .
Following the work by Nunes et al .
the degree of phase separation in segmented PU can be The main regions interested in the study are AeNH absorption peak at 3320 cm-1 was due to hydrogen bonded AeNH groups of urethane linkages.
The hydrogen bonding was constituted as proton donor and the oxygen in carbonyl of the hard segment and in ether linkages as soft segment.
The formation of hydrogen bonding by AeC=O group can be determined by examining the peak position at 1709 cm-1 for hydrogen bonded AeC=O and at 1731 cm-1 for free Ae C=O similar results were reported by Chen .
Figure 3 Thermo Haake Polydrive machine RESULTS AND DISCUSSION This chapter presents the result and discussion of the synthesis of polyurethane based on palm oil polyol, preparation of untreated clay to be clay nanocomposites with difference surfactants i.
trimethyl ammonium bromide (CTAB) and Octadecylamines (ODA), synthesis of polyurethane based on palm oil polyol as metric with clay nanocomposites as reinforcement, and determine the efficiency of thermal resistance of polyurethane/ clay thermogravimetric analysis (TGA).
The result of investigation to determine the micro-domain structures of segmented PU and PU/clay nanocomposites were evaluated by fourier transform infrared spectra (FTIR).
The mechanical properties in term of their tensile properties, including the dynamic mechanical properties of pure polyurethane (PU) and PU/clay nanocomposites, were Wide angle x-ray diffraction techniques were utilized to explore the extent of dispersion of clay in filled systems.
Furthermore, the molecular weights of materials were determined by Gel Permeation Chromatography apparatus.
Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X gives dispersity value of 1.
From the data also show the result of Mz was about 1256.
The Mw value that is vital in the synthesis of PU, i.
, the isocyanation process between polyol.
MDI and 1,4-BDO.
The molecular weight (M.
of PU based on palm oil was about 3266 [ Figure 4.
Mn of the products has become 1425 and Mz become 10090.
The corresponding dispersity value is 2.
That is, there is an overall increase in the molecular weight of the sample synthesized.
The increase molecular weight value indicating that product is high polymers.
The value in determining the different molecular-weight averages is related to the influence the various molecular-weight fractions have on properties and behavior (Gopakumar and Gopinathan, 2.
For high-molecular polymer chains may change the flexibility of the polymer to a much greater extent than the same number of low-molecular chains in the material.
Raising the molecular weight to higher power in the calculation of Mz than in the calculation of Mn reflects the greater influence of these longer chains.
Mz is related to elongation and flexibility, while Mn is related to brittleness and flow Meanwhile Mw is related to characteristics such as tensile strength and impact resistance (Lobo, 2.
The structure of the segmented polyurethane molecule can be classified into two phases: soft segment and hard segment.
Soft segment is obtained by reacting polyol and hard segment is coming from Hard segment associate into rigidity and hydrogen bonding, meanwhile soft segment most conjugated with flexibility (Petrovic and Ferguson, 1.
In the case of synthesis of polyurethane elastomers, the structure segmented polyurethane is important parameters for control of physical properties.
GPC is most measurements to determinant the segmented of polyurethane by calculated of molecular weight of the hard segment concentration (HSC) and calculated soft segment concentration (SSC).
Figure 4 The FTIR spectra of the synthesized polyol based on palm oil Figure 5 The FTIR spectra of the synthesis polyurethane based on palm oil polyol The molecular weight (MW) of polyol was obtained by using gel permeation chromatography (GPC).
The GPC is also termed size exclusion chromatography (SEC).
As suggested by the names, the mechanism of separation in GPC/SEC is based on apparent size differences among the sample components in solutions.
There are many techniques for determining the various molecular weight average [Lobo, 2.
such as Number average (M.
, can be obtained by membrane osmometry or endgroup analysis.
Weight average (M.
is determined by light scattering, while Z and Z 1 averages (Mz and Mz .
are measured by ultracentrifugation.
But GPC is unique in that all these averages can be obtained in a single analysis.
The GPC result of polyol is given in Figure 4 It shows that all the data of various molecular weight average appearance in the below of graphic.
The GPC data tabulated possesses the molecular weight averages was about Mw = 955 and Mn = 679.
This Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X The flexible .
segments in polyurethane elastomers greatly influence the elastic nature of the material and significantly contribute to its low temperature properties and extensibility.
Therefore the parameter of soft segment is highly important.
Furthermore crystallinity, if any, the melting point, and the possible ability to crystallize with strains, will also certainly influence the ultimate mechanical properties [Jia et al.
The hard segments in polyurethanes typically consist of an isocyanate and chainextender glycol or amine components.
Structure of the diisocyanate can have a critical influence on the properties of thermoplastic polyurethanes, such as highest levels of modulus, tear, and tensile.
The diisocyanate structure apparently influences the ability of the hard segments to pack more regularly and consequently to have higher intermolecular hydrogen bond interaction and s stronger physical network [Chun et al, 2.
PUs posses good mechanical properties such as high abrasion resistance, tear strength, flexibility and elasticity.
However, they also have some limitations by having lower thermal stability compared to other In order to solve this problem, we can employ modified clay montmorillonite (MMT) in the formulations for certain applications, because by adding minimum amount of MMT (<10 wt.
%) in the formulation, the mechanical and thermal properties of the composites could be enhanced significantly [Chen et al.
, 2.
Natural montmorillonite has a layered structure made up of disc shaped silicate layers with dimensions of approximately 100 nm in diameters, and 1 nm in thickness.
Montmorillonite based clay is hydrophilic and lacks affinity with hydrophobic organic polymers, ion exchange reactions of montmorillonite with various organic cations such as alkylammonium cations rendered the originally hydrophilic silicate surfaces hydrophobic.
If montmorillonite containing sodium ions between its layers is dispersed in water, it Figure 6 The GPC profiles of the polyol based on palm oil Figure 7 The GPC profiles of the synthesis polyurethane based on palm oil polyol Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X turns into a state in which the silicate layers swell uniformly.
If the ammonium salt of alkylamine is added to this aqueous mixture, then the alkylammonium ions are exchanged with the sodium ions.
As a result of this reaction, clay forms in which the alkylammonium ions are intercalated between the layers.
Because the silicate layers in the clay are negatively charged, they bond with the alkylammonium ions through ionic bonding if an ammonium salt is injected.
If the length and type of the alkyl chain are changed, the hydrophilic and hydrophobic characteristics and other characteristics of this organophilic clay can be adjusted such that surface modification of the clay becomes possible.
Furthermore the replacement of inorganic exchange cations by organic sodium ions can cause the clay The WAXD was used to examine the extent of dispersion of clay in the filled It was also used to measure the silicate layers distribution of the modified clays in the polymer matrix.
The montmorillonite (Kunipia-F or termed puremon.
that was modified with cetyltrimethyl
(CTAB)
octadodecylamine (ODA) are termed CTAB-mont and ODA-mont.
In Figure 4.
the d-spacing in CTAB-mont and ODAmont are 1.
571 nm and 1.
798 nm, respectively, being larger than that of the pure-mont, 1.
142 nm.
These indicate that both CTAB and ODA were successfully intercalated into the silicate layer.
homogeneously in water, but it does not blend direct in polymer because montmorillonite is too hydrophilic.
The hydrophilicity of montmorillonite should be reduced to allow blend in polymer.
montmorillonite has an excess negative charge, it can be combined with organic montmorillonite with organic cations.
The scheme is shown in Figure 8
Figure 8 The WAXD pattern of pure-PU
Figure 10 The WAXD pattern of CTABmont-PU
2000 oA
H2 O
Na -type montmorillonite Intercalating Montmorillonite PUs Organophilic montmorillonite Figure 9 Dispersive Figure 8 and 9 present three series WAXD curves of CTAB-mont-PU and ODA-montPU that were corresponded to polyurethane clay nanocomposites based on palm oil.
that graphs the appearance of WAXD peaks .
A = 2-10.
in 1, 3, and 5% CTAB-montPU indicated that these organoclay were completely intercalated in polyurethane as The similar results were obtained for 1, 3, and 5% ODA-mont-PU and as shown in Figure 3.
8, the intercalated could also be Na type montmorillonite is composed of sodium ions and negatively charged Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X either the organic modified silicate layers did not react with the PU molecules or reactions between organic modified silicate layers, thus indicating that PU did not cause any detectable change by FTIR.
Figure 11 The WAXD pattern of ODAmont-PU In the case of 1% CTAB-mont-PU, a very small peak was observed at 2A = 4.
spacing = 1.
With the increasing the clay content, the peak becomes stronger and exhibits a sharp increased peak toward the dspacing 2.
055 nm for 5% CTAB-mont-PU.
From the calculation, it was clearly shown that the interlayer spacing of ODA-mont-PU is higher than CTAB-mont-PU.
The different swollen spacing in these two organoclays are attributed to the respective size of the swelling agent, with the size of octadodecylamine being larger than of cetyltrimethyl ammonium bromide [Chen et , 2.
Table 3.
1 summaries the dspacing and 2A .
for CTAB-montPU and ODA-mont-PU.
Table 3.
1 :Summary of the d-spacing .
and 2A .
for Pure Kunipia.
CTABmont.
ODA-mont.
CATB-mont-PU and ODA-mont-PU Figure 12 The FTIR spectra of pure PU and 1,3,5% CTAB-mont-PU Figure 13 The FTIR spectra of pure PU and 1,3,5% ODA-mont-PU Therefore, the effect of the intercalated silicate layers on the degree of phase separation in polyurethane can be determined solely from the extent of hydrogen bonding in the hard segments and the degree of hydrogen bonding in these polyurethane nanocomposites can be obtained from their IR spectra also.
From the investigation by Pattanayak and Jana .
that has been studied the nature and behavior of hydrogen bonding in segmented polyether and polyester urethane elastomers, it has been concluded that at 3320 cm-1 peak and 3480 cm-1 peak in the IR spectra of pure PU are due to hydrogen bonded AeNH groups and free AeNH groups The microdomain and the hydrogen bonding of segmented PU and the PU/clay were analyzed FTIR.
It was found that the positions of peaks for distinctive functional groups in the IR spectra of the pure PU and PU/clay nanocomposites are identical, which means that the chemical structures of polyurethane had not been affected by the presence of organoclay, which implied that Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X The hydrogen bonding was constituted by the AeNH groups being as proton donor and oxygen in carbonyls of the hard segment and in ethers of the soft segment as proton acceptors.
The formation of hydrogen bonding can be determined by examining the peak position of free urethane carbonyl and hydrogen bonded carbonyl.
The peak at 1733 cm-1 is assigned to free the urethane carbonyl, while the peak at 1703 cm-1 is due to hydrogen bonded carbonyl [Tien and Wei, 2001 .
Dai et al.
, 2.
The standard assignment of vibration modes the absorption band of these groups are listed in Table 3.
Table 3.
2 : Assigments of the Absorption Bands in FT-IR Spectra of Polyurethane .
odified from Pattanayak and Jana .
Tien and Wei, 2001 .
Dai et al.
, 2004 )
by using Eqs.
, respectively [Chen et al.
, 2.
Cbonded A.
DPS A
Cbonded A C free R A 1 DPM A1 A DPS a.
Table 4.
Absorption of carbonyl and degree of phase separation Based on these calculations, the DPS and DPM organoclay/PU nanocomposites are given in Table 4.
indicated in Table 4.
3, the phase separation ratio in pure PU is about 52%.
There was almost no change in DPS and DPM of all CTAB-mont/PU ODA-mont/PU nanocomposites, indicating no dependence on the amount of added organoclay.
This can be explained by an uniform dispersion of intercalated silicate layers of organoclay in the nanometer scale in PU matrix, which cannot be matched by the classical composite materials.
Similar phenomena were also observed by Pattanayak and Jana .
Gorrasi et.
The MW of pure PU and PU/ clay nanocomposites are given in Table 4.
Pure PU had MW of 3915.
19, 1% CTAB-montPU had MW of 4160.
33, 3% CTAB-montPU had MW of 4360.
29 and 5% CTABmont-PU had MW of 4417.
25 while 1% ODA-mont-PU had MW of 4245.
12, 3%
ODA-mont-PU had MW of 4429.
45 and 5% ODA-mont-PU had MW of 4610.
In each case, corresponding to the fact that the segmented PU structures were affected by the presence of organoclay as identified by their FTIR spectra, the molecular weight of pure PU and PU/ clay nanocomposites in general were not strongly affected by the addition of organoclay, this result is similar with the research by T.
-K.
Chen et al .
The degree of the carbonyl groups participating in hydrogen bonding can be described by the carbonyl hydrogen bonding index.
R, as given in Eq.
Au R A bonded bonded A 1703 a.
C free Au free
A1733
where A is the intensity of the characteristic absorbance.
C is the concentration and Aubonded and Aufree are the extinction coefficients of the bonded and the free carbonyl groups.
The value of Aubonded / Aufree was 0 and 1.
2 [Jia et al.
Rekondo et al.
In this study, the value of Aubonded / Aufree is taken as 1.
0, and the carbonyl hydrogen bonding index is directly equal to the ratio of the normalized absorbance intensity in 1703 cm-1 to that in The degree of hard segment linking hard segment .
egree of phase separation.
DPS) and the degree of hard segment linking soft segment or silicate layers .
egree of phase mixing.
DPM) can be obtained readily Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X Table3.
4:Thenumber-average molecular weight and mechanical properties of Pure PU and PU/clay nanocomposites As shown in Table 3.
4, and Figure 3.
11, the ultimate strength was increased dramatically with the increasing of the organoclay content and has reached maximum values at 5 wt% organoclay content with the increase of the tensile strength of more than 214.
63 % by the addition of only 5% of the montmorillonite CTAB-mont and ODAmont respectively.
Furthermore Table 4.
and Figure 15 also illustrate that the elongation at break of the nanocomposites were increased with the addition of organoclay content, which means it was related to the interaction between the pure PU and treated clays [Xiong et al, 2.
The graphics in Figures 14 and 15 also explains that the tensile strength and elongation at break value of the polyurethane containing octadodecylamine (ODA-mon.
was usually higher than that of cetyltrimethyl ammonium bromide (CTABmon.
, it was indicated a strong effect of ODA-mont Most applications of elastomers would be impossible without the reinforcement of certain fillers, such as carbon black, clay.
Reinforcement is usually associated with improvement in modulus, hardness, and tensile and tear strength of vulcanized The modulus reinforcement of Pus-clay nanocomposites was examined using Guth.
Halping-Tsai and the modified Halping-Tsai equations, which are universally used for composites reinforced by fiber-like or rodlike filler.
Experiments have been performed to measure YoungAos modulus of the nanocomposites in the direction of the Pus-clay The results are shown in Table 3.
5 : Measured tensile modulus E for Pus-clay nanocomposites The mechanical properties of PU and PU/clay nanocomposites are given in Table 4.
Figures 14 and 15.
The modified organoclay had a remarkably beneficial effect on the strength and elongation at break of the nanocomposites, which both increased with increasing clay content, the ODA treated varieties having the highest The fact that the elongation at break of the nanocomposites increased with the organoclay content suggests that elongation was related to the interaction between the pure PU and the treated clays [Rihayat et al.
Figure 14.
Tensile strength of pure PU and PU/clay nanocomposites Figure 15 Elongation at break of pure PU and PU/clay nanocomposites Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X Figure 16 compares experimental modulus data of 1,3, 5 wt% of CTAB-mont-PU and ODA-mont-PU, respectively, with the model predictions using the parameter values in Table 4.
The results show that the predictions by Guth equation agree very well with the experimental data.
whereas the HalpinAeTsai equation can only be applied to predict the modulus of rubberAeclay nanocomposites in the range of low clay volume fractions, for example, less than 1 The theoretical prediction for modulus behavior investigated above suggested that the resulting aspect ratio of 1000, with 3 wt% clay for example, is a contributing reinforcing factor.
Such high aspect ratio silicate platelets could be present in exfoliated systems where individual platelets separate from the clay stack and are dispersed in the polyurethane In order to see if this is the case, xray diffraction (XRD) was conducted to explore the microstructure of PUsmontmorillonite composites.
Table 3.
5 showed the summarized of tensile The enhancement of tensile modulus is directly attributed to the reinforcement provided by the dispersed silicate layers and YoungAos modulus can also be affected by the interfacial interaction between silicate layers and polyurethane Therefore.
YoungAos modulus increased with increasing the clay content and the dispersibility of organoclay.
The largest increase in YoungAos modulus .
550 MP.
was shown at 5% ODAmont-PU.
As mentioned above, there are polyurethane matrix and layered silicates such as the hydrogen bonding and the chemical bonding, so the tensile strength and elongation at break increased by introducing organoclay.
Because the interfacial area between organoclay and polyurethane matrix became larger and the interaction between organoclay and polyurethane matrix became also stronger, the tensile modulus of ODA-mont-PU was significantly higher than that of CTABmont-PU and pure polyurethane.
The dynamic mechanical analysis (DMA) was performed to examine the effect of the clays on the structure, concentration and organization of the hard-segments, and their interaction with the soft segments, have a dominant influence on the physical and mechanical properties of the urethane polymer [Abdalla et al, 2.
The loss factors .
an A) value of pure PU and PU/clay nanocomposites are presented in Figure 3.
Figure 16 Experimentally modulus and theoretical predictions by two different models : Guth and Halpin-Tsai equations for .
CTAB-mont-PU and .
ODA-mont-PU.
According to the Halpin-Tsai theory of filler reinforcement, volume fraction and aspect ratio are key parameters governing the mechanical properties of composites.
the formation of nanocomposites, clay platelets initially stacked together to form clay particles are intercalated with polymer, exfoliated and dispersed in the polymer A single platelet layer is sheet like, having a thickness of only about 1 nm and lateral dimensions that are typically on the order of 500-2000 nm [Ray and Okamoto.
Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X Treated clay seems to be more efficient for increasing the glass transition temperature (T.
According to Choi et al .
and Agag et al .
, it was confirmed that the Tg increase with the increased of the clay content resulting from the confinement effect of clay to polyurethane molecules and the strong interactions of hydrogen bonding in between the urethane groups of polyurethane molecules and oxygen atoms on the surface of organoclay.
In Figure 3.
14, the Tg of CTAB-mont-PU 776oC, -8.
113oC and -6.
764oC for clay content of 1%, 3% and 5%.
Those values are higher than pure PU which was: -12.
But in fig 15 the Tg of ODA-mont-PU is higher than the Tg of CTAB-mont-PU with the results .
or the ODA-mont-PU sampl.
114oC , -6,5oC and -5oC at the similar clay contents respectively.
degradation process usually passes through three stages.
In the first and second stage, the urethane bonds decompose to form alcohols and isocyanates.
Complete volatilisation of resulting chain fragments is prevented by dimerisation of isocyanate to carbodiimides, which react with the alcohol groups to give relatively stable substituted ureas .
econd ste.
that decompose in the third stage.
Trimerisation of isocyanates may also occur under certain conditions to yield thermally stable isocyanurate rings.
The final step is the high temperature degradation of these stabilized structures to yield volatile products and a small quantity of carbonaceous char.
The TGA analysis of pure PU.
CTAB-mont 1, 3, 5 wt% and ODA-mont-PU 1, 3, 5 wt%, respectively, are shown in Figure 4.
16 and 4.
With regard to pure PU , the degradation at 200400 oC is attributed to depolycondensation Then at higher temperature, the material degrades slowly, and it degrades completely at about 700oC.
The results show that thermal resistances are enhanced in the presence of clay compared to pure PU.
This indicates an improvement in thermal stability of PU because the organic material can prevent the heat from expanding quickly and limit the further degradation.
Onset degradation of pure PU is at 200oC, and is lower than of the CTAB-mont-PU and ODA-mont-PU takes place at about 318oC and 330oC.
It means the thermal resistance of nanocomposites improved above 62% compared pure polymer.
But in overall thermal resistance of ODA-mont-PU nanocomposites was much higher than that of pure PU and CTAB-mont-PU.
Figure 3.
DMA curves for tan A of pure PU and CTAB-mont-PU 1, 3 , 5 wt% Figure 3.
DMA curves for tan A of pure PU and ODA-mont-PU 1,3,5 wt% The thermal properties were determined using Thermogravimetric analysis (TGA).
During a ramped heating under nitrogen, such as in a TGA experiment, the Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X Only single heating rate, pseudo first order method has been applied in this study.
Figures 4.
24 show the plot of Ln [.
w/d.
against -1/T for the pure PU and PU/ clay nanocomposites 1, 3, 5 wt%, respectively, on the basis equation .
from section 3.
8 (Chapter .
, if the reaction is first order, it should be expected that the data calculated from TGA thermograms base on equation .
could be fitted by a straight line of the slope equal to activation energy.
E, and intercept equal to Ln A, where A is pre-exponential or frequency factor.
The values of E and A calculated following the approach described above are summarized in Table 4.
The E value of the materials can be used to determine whether the initial degradation step [Gu and Liang, 2.
As can be seen from Table 4.
6 the clay had a great effect on activation energy of nanocomposites and pristine polyurethane, especially for 5 wt% CTAB-mont PU and 5 wt% ODA-mont PU.
Table 3.
6:A summary of the kinetics parameters obtained using the simple linear regression method.
Figure 4.
The TGA curves of pure PU and PU/clay nanocomposites CTAB-montPU 1, 3, 5 wt% Figure 4.
The TGA curves of pure PU and PU/clay nanocomposites ODA-montPU 1,3,5 wt% From the graphic analysis showed of CTABmont-PU and ODA-mont-PU in the temperature range from 100 to 275 oC, the PU/clay nanocomposites contain swelling agent (CTAB and ODA) degrades slightly faster than pure PU, especially in 1 and 3 This is because the amount of CTAB and ODA used increased with the amount of organoclay in PU.
These small organic molecules tend to degrade before the PU polymer, causing a slight weight loss in the After decomposition of the swelling agent, the PU/clay nanocomposite displayed higher thermal resistance than that of PU in the temperature range above 400oC because of the presence of clay.
This indicating inorganic material can prevent the heat to expand quickly and limit the further From the data clearly indicate that the long chain molecular motion in the PU-clay nanocomposites encounters a markedly larger energy barrier than it does in pure PU.
That is at the same temperature the molecular mobility than the pure polymer.
Because the molecular mobility is the major factor that contributes to the transport of reactive species .
, oxygen and or/or radical.
within the polymer, the nanocomposite is likely to have lower reactivity and, therefore, greater chemical and thermal stability than pure PU [Vyazovkin et al, 2.
Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X Ln[(-dw/d.
Ln [(-dw/d.
y = -224.
R2 = 0.
y = -183.
R = 0.
-1/T
-1/T
Figure 3.
18: First order kinetic plot for pure Polyurethane Figure 3.
22: First order kinetic plot for PU/Clay nanocomposites ODA 1 wt% y = -172.
R2 = 0.
Ln [(-dw/d.
Ln[(-dw/d.
y = -190.
R2 = 0.
-1/T
Figure 3.
19: First order kinetic plot for PU/Clay nanocomposites CTAB 1 wt% -1/T Figure 3.
23: First order kinetic plot for PU/Clay nanocomposites ODA 3 wt% Ln[(-dw/d.
y = -188.
R2 = 0.
Ln [(-dw/d.
-1/T Figure 3.
20: First order kinetic plot for PU/Clay nanocomposites CTAB 3 wt% y = -236.
R2 = 0.
Ln [(-dw/d.
-1/T y = -224.
R2 = 0.
Figure 3.
24: First order kinetic plot for PU/Clay nanocomposites ODA 5 wt% In figures 3.
25 and 3.
26, morphological observations on the fractured surfaces of the PU and PU/clay nanocomposites samples are shown.
The filler employed as reinforcements for polymers and resins are invariably coated with sizing resin whose role to protect them during handling and Furthermore the filler surface is treated to provide chemical interactions with the polymer employed as the matrix.
The net result of SEM is that the nature of -1/T Figure 3.
21: First order kinetic plot for PU/Clay nanocomposites CTAB 5 wt% Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X differing interactions such as the physical mixing of the matrix and sizing resins and the nature of chemisorptions at the filler surface gives rise to a interphase region as opposed to a distinct interface between nanoclay and polymer matrix [ Lam et al, the polymeric matrix and the filler [Wambua et al, 2.
The interface between fiber and matrix is shown below in Figure 3.
In Figure 3.
26 show ODA-Mont- PU 3 wt% has a good dispersion between matrix and Duquesne et al.
studied the better dispersion between nanoclay and polymer matrix.
The bright spots on the backscattered images correspond to clay Figure 3.
26 presents the microstructure of a nanocomposite with 3 wt% of organoclay.
The clay particles are finely dispersed in the material.
Moreover, the finest dispersion can probably not be detected by SEM.
Apparently, the clay particles are more finely dispersed in the nanocomposite as compared with in the conventional composite.
This difference must be due to the treatment of the clay.
The alkylammonium ions render the clay organophilic and allow a better dispersion of the clay in an organic medium.
Small particle aggregates are observable at relatively low magnification.
Figure 3.
32 shows the transmission electron micrograph of sections of the PU/Clay nanocomposites.
The dark lines are intersections of silicates layers, and the other region is PU matrix.
It can be seen that silicate layers have reached nanometer scale and effectively intercalated or exfoliated in the PU matrix.
Observations of the micrograph reveal that each dark line often corresponds to several clay layers [Kornmann et al, 2.
In some cases, this is because the layers are closely stacked together, suggesting the absence of alkylammonium ions in the galleries.
The TEM image of the PU/clay nanocomposites showed that the clay particles were broken into small tactoids and uniformly dispersed in the PU matrix, which resulted from strong interaction between clay and polymer and it is imperative that the surface polarities of the polymer and clays or organoclays be matched [Park et al, 2.
Figures 3.
27 and 3.
TEM photograph of PU/Clay nanocomposites CTAB 1 wt% and ODA 1 wt% show that clay layers are completely intercalated when 1% clay were Figure 3.
SEM micrographs of interfacial adhesion between nanoclay and matrix PU Figure 3.
SEM micrographs of a good dispersion between nanoclay and ODAMont- PU 3 wt% Jayaraman .
studied the fibers and matrix must corporate for a composite to be an effective load bearing.
This corporation between the fillers and matrix will not exist without the presence of the interface.
The interface acts as a binder and transfer load between the matrix and the reinforcing Further, because each filler forms an individual interface with the matrix, the interfacial area is very large.
The interface, therefore, plays a key role in controlling the mechanical properties of a composite.
The role of the matrix in the fiber-reinforced composite is to transfer the load to the stiff fiber through shear stress at the interface.
This process required a good bond between Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X added into PU matrix.
Figures 3.
29 and 3.
exhibits a well-intercalated and exfoliated At the other image in figures 3.
32, show fine and almost uniform distribution of clay particles in the PU matrix where the clay particles exhibit both stacked and flocculated to the sample surface and an intercalated structure has been produced.
The presence of exfoliated clay layers at higher concentration probably caused by high shear impact on the mixture.
As shear mixing progress, the molten polymer becomes more and more viscous with the dispersion of clay particles.
higher clay content the viscosity will help the delamination of silicate layers and also intercalation of the polymer chains into the silicate layers therefore increase the basal spacing of clay platelets in the PU matrix (Fornes et al.
, 2.
Figure 3.
TEM photograph of PU/Clay nanocomposites CTAB 3 wt% Figure 3.
TEM photograph of PU/Clay nanocomposites ODA 3 wt% Figure 4.
TEM photograph of PU/Clay nanocomposites CTAB 5 wt% Figure 3.
TEM photograph of PU/Clay nanocomposites CTAB 1 wt% Figure 4.
TEM photograph of PU/Clay nanocomposites ODA 5 wt% CONCLUSION Isocyanate groups .
NHCO-O-) .
olyethers, polyester, etc.
) are required as reactants for the production of high molecular weight polyurethane elastomers (PU.
PUs are very significant goods that have great mechanical and elastic qualities, high hardness for a given modulus, and strong abrasion and chemical resistance.
The majority of the hydroxyl groups, also known Figure3.
TEM photograph of PU/Clay nanocomposites ODA 1 wt% Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X as polyols, now utilized to make polyurethane come from petrochemical Mineral oil, which is a finite resource whose supply has only been anticipated to last for about 50 years in optimistic projections, is the source of petrochemical Other potential sources should be found or investigated sooner or later.
Since about 80% of the world's production of renewable sources is based on plant oils, such as soybean oil, palm oil, sunflower oil, olive oil, and seed oils, among others, the options used in this research work to use palm oil as a raw material in polyol synthesis are quite interesting.
Glycerol and palm oil .
ought from a local manufacture.
based on oleic acid were combined to create polyols.
The polyols could also be utilized as starting materials for the isocyanation of isocyanate compounds to produce polyurethanes.
FTIR spectroscopy was used to track the production of polyol from glycerol and oleic acid derived from palm oil.
Gel permeation chromatography (GPC) was used to determine the molecular weight (MW) of polyol, and the result was around 950.
Following Seymour et al.
's research, the segmented PU microdomain structures were examined by FTIR to determine the degree of phase separation.
By comparing the peak positions at 1709 cm-1 for hydrogen bound -C=O and at 1731 cm-1 for free -C=O, it is possible to ascertain the establishment of hydrogen bonding by the -C=O group.
The molecular weight (MW) of the palm oilbased PU was around 3.
Because of ion exchange interactions between montmorillonite and other organic cations, such as alkylammonium cations, the initially hydrophilic silicate surfaces became hydrophobic, making montmorillonitebased clay hydrophilic and lacking affinity for hydrophobic organic polymers.
The silicate layer distribution of the modified clays in the polymer matrix was examined using the WAXD, and the degree of clay dispersion in the filled samples was also The terms "CTAB-mont" and "ODA-mont" refer to the montmorillonite (Kunipia-F or "pure-mont") that has undergone chemical modification using cetyltrimethyl ammonium bromide (CTAB) and octadodecylamine (ODA).
As a result, the d-spacing of CTAB-mont and ODAmont is bigger than that of pure-mont, which 142 nm, at 1.
571 nm and 1.
798 nm.
These show that the silicate was successfully intercalated with both CTAB and ODA.
The morphology, mechanical and thermal properties that have been investigated in this study were corresponded to the disperse of organoclay in the polyurethane matrix.
The treated clays were completely intercalated in polyurethane matrix and the intercalation effects were increased with the increasing of the clay contents.
In the appearance of WAXD peaks .
A = 2-10.
in 1, 3, and 5% CTAB-mont-PU indicated that these organoclay were completely intercalated in polyurethane as matrix.
The similar results were obtained for 1, 3, and 5% ODA-montPU.
The microdomain and the hydrogen bonding of segmented PU and the PU/clay were analyzed FTIR.
It was found that the positions of peaks for distinctive functional groups in the IR spectra of the pure PU and PU/clay nanocomposites are identical, which means that the chemical structures of polyurethane had not been affected by the presence of organoclay.
The mechanical properties of PU and PU/clay nanocomposites were studied in this work.
It was found that the modified organoclay content had a remarkable effect on the strength of the nanocomposites.
The tensile strength and elongation at break increased more than 200%, which could be assumed as a result of the strong interaction between treated clay and polyurethane as The dynamic mechanical analysis was employed to examine the effect of clay contents on the thermomechanical properties and microstructure of the material and it was found that, the glass transition (T.
was increased with the increasing of the clay contents, which was assumed as a result of the confinement effects of clay to polyurethane molecules and the strong Jurnal Reaksi (Journal of Science and Technolog.
Jurusan Teknik Kimia Politeknik Negeri Lhokseumawe Vol.
21 No.
Juni 2023 ISSN 1693-248X interactions such as hydrogen bonding polyurethane molecules and oxygen atoms on the surface of organoclays.
The thermal properties were determined using TGA.
The TGA analysis of pure PU.
CTAB-mont 1, 3, 5 wt% and ODA-mont-PU 1, 3, 5 wt%, respectively.
With regard to pure PU, the degradation at 200-400 oC is attributed to depolycondensation reaction.
Then at higher temperature, the material degrades slowly, and it degrades completely at about 700oC.
The results show that thermal resistances are enhanced in the presence of clay compared to pure PU.
This indicates an improvement in thermal stability of PU because the organic material can prevent the heat from expanding quickly and limit the further degradation.
Onset degradation of pure PU is at 200oC, and is lower than of the CTAB-mont-PU and ODA-mont-PU takes place at about 318oC and 330oC.
It means the thermal resistance of nanocomposites improved above 62% compared pure polymer.
Morphological observations on the fractured surfaces of the PU and PU/clay nanocomposites samples were determined by SEM and TEM.
The result show clay particles are finely dispersed in the material.
Journal materials scence 39: 1919-1925 Agag.
Koga.
and Takeichi.
Studies on thermal and mechanical properties of polyimide-clay Polymer 42:
Alexandre.
M and Dubois.
Polymer-layered properties and uses of a new class of materials.
Materials Science and Engineering: R: Reports 28: 163 Alexandrovich.
Karasz.
Macknight.
Dielectric study of polymer compatibility:
Blends of polystyrene/poly-2ehlorostyrene.
Macromolec.
Sci.
Phys.
B17: 501.
Anseth.
Bowman.
and Peppas.
Mechanical properties Biomaterials 17.
Assink.
The study of domain structure in polyurethanes by nuclear magnetic resonance.
Polym.
Sci.
Polym.
Phys.
Ed.
REFERENCES