924
Indones.
Chem.
, 2023, 23 .
, 924 - 936
Fabrication of Dye Sensitized Solar Cell (DSSC) Using Combination of Dyes Extracted from Curcuma (Curcuma xanthorrhiz.
Rhizome and Binahong (Anredera cordifoli.
Leaf with Treatment in pH of the Extraction Pirim Setiarso*.
Rifanda Viantiano Harsono, and Nita Kusumawati Department of Chemistry.
Faculty of Mathematics and Natural Sciences.
Universitas Negeri Surabaya.
Jl.
Ketintang.
Surabaya 60231.
Indonesia * Corresponding author:
email: pirimsetiarso@unesa.
Received: September 20, 2022 Accepted: June 8, 2023 DOI: 10.
22146/ijc.
Abstract: Research on Dye Sensitized Solar Cell (DSSC) fabrication has been carried out using a combination of dyes extracted from Curcuma xanthorrhiza and Anredera Each dye was extracted by treating pH 1 to 13 and then characterized using UV-Vis spectroscopy.
The band gap energy was determined by using the cyclic voltammetric method.
The UV-Vis spectrum of C.
xanthorrhiza extract reveals the presence of curcumin components.
The UV-Vis spectrum of A.
cordifolia indicates the presence of chlorophyll and a trace of anthocyanin.
xanthorrhiza extract had the least band gap energy in the acid phase, pH 1, at 0.
66 eV, and the alkaline phase, pH 13, at 43 eV.
The minimum band gap energy of A.
cordifolia extract was determined to be 96 eV in the acid phase, pH 7, and 0.
65 eV in the alkaline phase, pH 12.
When A.
cordifolia and C.
xanthorrhiza extracts were mixed, with the best composition ratios being pH 7:pH 1 .
:2 OO pH 1.
and pH 12:pH 13 .
:4 OO pH 12.
The composition of this mixture was applied to the DSSC resulting in an efficiency of 0.
096 and 0.
Keywords: Curcuma xanthorrhiza.
Anredera cordifolia.
DSSC
n INTRODUCTION The demand for energy around the world is increasing every day, and this trend will continue in the Therefore, efforts to develop renewable energy sources continue to be made, such as energy from the sun, wind, and water, which are widely available in nature at low cost .
This motivates researchers to explore energy sources that are clean, practical, renewable, abundant, and environmentally friendly.
One of the promising renewable energy sources is solar cells, also known as photovoltaic solar cell to harvest solar energy .
Solar energy is one of the energies that can be converted into other energies .
Sunlight can be converted into electrical energy using solar cells by converting solar radiation directly into a source of electrical energy .
Dye Sensitized Solar Cells (DSSC) were first discovered by Michael Grytzel and Brian O'Regan in 1991.
DSSC continues to develop until the manufacture of Pirim Setiarso et al.
Nitrogen-doped carbon nanotubes grafting rutile TiO2 nanofilms, which is carried out by Belkhanchi et al.
The DSSC device consists of a conductive glass, a semiconductor oxide material, a dye as a photosensitizer, an electrolyte, and a counter electrode .
Currently, the most efficient dye sensitizer used for electron transfer in DSSC is a polypyridyl ruthenium(II) complex compound, with an overall photovoltaic conversion efficiency of 10% .
DSSC
has attracted wide attention both scientifically and industrially due to their easy manufacture, low cost, versatility, and wide range of dyes .
The working principle of DSSC will be briefly explained as follows.
Sunlight with a certain intensity can penetrate into the dye layer because the layer of conductive glass and semiconductor crystals can be easily penetrated by visible light.
If the energy of the photon hits the energy gap of the dye molecule, which is the difference between the highest electron-filled Indones.
Chem.
, 2023, 23 .
, 924 - 936
molecular orbital (HOMO) and the lowest empty molecular orbital (LUMO), the dye will absorb it, promoting one electron from HOMO to LUMO.
The light energy can cause the excitation of one electron from HOMO to LUMO in the dye molecule.
The excited electrons will then be injected into the conduction band of the semiconductor then collected by the conductive glass of the anode.
These electrons flow towards an inert counter electrode and are collected by the conductive glass at the cathode.
Then the electrons will be captured by the redox pair electrolyte and will return to the dye for regeneration .
An illustration of the working principle of DSSC is shown in Fig.
Recently, many DSSC studies have explored sources of natural dyes as promising sensitizers.
Besides being easy to obtain, natural dyes are also cheap and environmentally friendly.
Natural dyes could come from plants, such as flowers, leaves, fruit, fruit skins, and Natural pigments that have been studied to date include anthocyanins, chlorophyll, betacyanins, betaxanthins, betalains, and beta-carotene .
Natural dyes can be extracted directly from plants with a variety of solvents and a variety of treatments.
DSSC fabricated using extracts from plants of saffron, mallow, red onion, and oregano has an efficiency of 0.
51, 0.
45, 0.
54, and 0.
Previous studies have also reported that DSSC fabricated using extracts from pandan leaves has an efficiency of 0.
35% .
and spinach leaves of 0.
002% .
Many studies in the world also focus research on semiconductor materials.
Research on semiconductors is expected to increase the efficiency of DSSC, which also considers the dye molecules that can easily bind to the Until now, the most frequently used semiconductor is TiO2 because it is stable, easy to obtain, and non-toxic .
In addition, the dye can also bind easily to the TiO2 layer to improve the performance of the DSSC.
Semiconductors besides TiO2, there are also other materials such as ZnO .
SnO2 .
ZnO-CdS .
ZnO-Fe2O3 .
, and TiO2-Ag .
The purpose of this study was to determine the performance efficiency of DSSC using dyes extracted from Curcuma xanthorrhiza and Anredera cordifolia.
Each sample was optimized for pH in the extraction process to determine the smallest band gap energy.
From here, the smallest band gap will be varied in the mixing composition, and the smallest band gap energy will be sought again.
Then, it will be used for DSSC fabrication.
Measurement of band gap energy using Cyclic Voltammetry (CV) method, and for the characterization of compounds using UV-Vis spectrophotometry.
n EXPERIMENTAL SECTION Materials TiO2 powder obtained from Sigma Aldrich.
NaOH.
KI, and polyethylene glycol (PEG 1.
were purchased from Merck.
Demineralization water purchased from CIMS.
Ethanol and acetonitrile were purchased from Fulltime.
xanthorrhiza rhizome and A.
cordifolia leaves were bought from local markets in Pabean-Surabaya, with curcumin concentration varying from 1.
0Ae2.
4% in the extract of C.
xanthorrhiza rhizome and chlorophyll content ranging from 20 to 24 mg/L in the extract of A.
Carbon pencil 2B (Faber-Castel.
Kimwipes KIMTECH (PT Indolab Utam.
and cudle wax (Aladin.
PT Elos Bintang Selama.
Iodine (I.
was purchased in VWR Chemicals.
ITO conductive glass was purchased from Ali Jaya Lab.
HNO3 was obtained from Emsure while HCl was purchased from SAP Chemicals.
Instrumentation Fig 1.
Working principle of DSSC .
Pirim Setiarso et al.
Calibrated digital pH meter (ATC), used to adjust A rotary evaporator (Buchi R-.
is used to evaporate the solvent resulting from the extraction.
UVVis spectroscopy (Shimadzu 1.
was used to Indones.
Chem.
, 2023, 23 .
, 924 - 936
characterize the compounds produced from the extraction of C.
xanthorrhiza and A.
The band gap energy was determined using a Voltammetry .
VA Computrac.
DSSC performance test using 10-watt LED lamp .
554 mW/cm.
, multimeter, potentiometer, and other supporting tools.
Procedure Extraction of C.
xanthorrhiza rhizomes The obtained C.
xanthorrhiza is then peeled off and washed with water until clean.
xanthorrhiza that has been cleaned, cut into small pieces, and then dried using an oven.
xanthorrhiza was extracted using the maceration method.
The dried C.
xanthorrhiza is reduced in size by breaking it, then macerated using ethanol with a ratio of 1:10 .
ample:solven.
Optimization of the extraction is done by adjusting the pH from 1 to 13.
Adjust the pH by adding HCl and NaOH.
Maceration was carried out in dark conditions and protected from light for A 24 h.
The extraction results were then filtered using filter paper.
The obtained filtrate is concentrated using a rotary evaporator.
Extraction of A.
cordifolia leaves The leaves were obtained from the A.
plant, which was separated from the stem.
Then the A.
cordifolia leaves were cleaned with a tissue that had been moistened with a little water and then cut into small The extraction process for A.
cordifolia leaves was the same as for C.
xanthorrhiza rhizomes.
Preparation of TiO2 paste TiO2 paste was prepared based on the procedure from previous research .
, with a slight modification by adding PEG 1000.
A 1.
15 g TiO2 powder was added with 1.
5 g PEG Then 1.
5 mL HNO3 was added to the mixture and stirred for A 30 min until evenly distributed.
After that, let it stand for A 10 min until the paste is stable.
Preparation of working electrode The working electrode was prepared following the procedure from previous work .
, with slight The prepared TiO2 paste was coated onto the ITO glass on the conductive side.
Paste the coating using the Doctor Blade method, with an area of 2 cm y 1.
5 cm.
Then the glass is heated at 450 AC using a Pirim Setiarso et al.
hot plate for 30 min.
The sintering product is left to stand until the temperature returns to normal.
TiO2 coating that exceeds the active area of 2 cm y 1.
5 cm is removed with ethanol-soaked laboratory wipes.
The finished glass is then soaked in color pigments extracted from C.
xanthorrhiza and A.
cordifolia for 24 h.
Soaking is done in a dark place away from light.
After soaking, color pigments that exceed the active area are removed with ethanol-soaked laboratory wipes.
Preparation of counter electrode The counter electrode was made following the procedure from previous research .
, with some ITO glass was made with a deposition size of 2 cm y 1.
5 cm using tape.
A 2B pencil graphite is shaded on ITO glass, then the tape is removed.
ITO glass which has been shaded with pencil graphite, is heated over a burning candle.
After that, wait until the temperature decreases, and trim the edges using ethanol-soaked laboratory wipes.
Preparation of electrolyte The electrolyte solution was made by dissolving 3 g of KI and 1.
27 g of I2 in 100 mL of ethylene glycol.
To avoid direct sunlight, the solution was stored in a dark place.
Assembly of dye-sensitized solar cell The DSSC circuit starts from the working electrode, then stacked with the opposing electrode, clamped left and right with a paperclip.
After that, the electrolyte solution is dripped on the edges, occasionally opening the paper clip gap to make it easier for the electrolyte to enter it.
Characterization and measurement The results of A.
cordifolia and C.
extracts which optimized for pH values, were divided into two ranges is at pH 1 to 7 .
onsidered as the acid phas.
, and at pH 8 to 13 .
onsidered as the alkaline phas.
Characterization of extracted compounds using UV-Vis Then the band gap energy is determined using CV method, with a potential range of -1 to 1 V and a scan rate of 20 mV/s.
Characterization of DSSC is determined from the value of Voc.
Isc.
Pin.
FF, and efficiency.
To test the Indones.
Chem.
, 2023, 23 .
, 924 - 936
performance of DSSC using a potentiometer 250 k.
For the light source, a LED lamp 10 watt is used with a light intensity of 509.
554 mW/cm2.
The overall performance of the cell was determined by FF.
The FF (Eq.
) and cell efficiency ( (Eq.
) were calculated using the following formula .
FF A max m ax
Voc C Isc
FF C Voc C Isc
C 100%
Pin where Vmax = maximum output voltage.
Imax = maximum output current.
Isc = short circuit current.
Voc = open circuit voltage, and Pin = input power 509.
554 mW/cm2.
n RESULTS AND DISCUSSION UV-Vis Spectroscopic Characterization Results of C.
xanthorrhiza extract with pH treatment did not show a significant shift in wavelength.
In the pH range of 1Ae7 (Fig.
), the resulting wavelength is around 424 nm.
This compound tends to be stable and maintains its structure in acidic conditions .
A peak with a maximum wavelength of 422 nm was found at pH 8Ae11 (Fig.
At pH 8Ae11 (Fig.
), the resulting wavelength is around 422 nm, pH 13 has shifted to 419 nm and there are signs of the appearance of small absorption at a wavelength of 438 nm.
This is a characteristic of curcumins in C.
Electron excitation of the AIeA* transition occurs in the absorption band in the visible light range, not the nIeA* transition, which is proven by theoretical studies .
Although not significant, curcumin at pH 8Ae12 experienced a hypochromic or blue shift effect caused by the influence of solvents.
At pH 13, a shoulder peak occurs at 438 nm.
Alkaline hydrolysis causes the degradation of curcumin, resulting in ferulic acid and feruloyl methane fractions, which reduce absorbance .
This is supported by the research of Sinha et al.
and Pourhajibagher et al.
who reported that curcumin extracts in ethanol show variable wavelengths around 350Ae470 nm due to the degradation of curcumin compounds at the pH UV-Vis Spectroscopic Characterization Results of the A.
cordifolia extract will be presented in this study.
Treatment of pH extract under acidic conditions did not show a significant wavelength shift.
can be seen in Fig.
, the treatment of pH 1Ae7 on the extract showed the same peak pattern.
The absorption peaks appear at 664, 436, and 412 nm, which reflect the characteristics of the chlorophyll a .
Theoretically, chlorophyll will lose the central magnesium atom in its structure under acidic conditions, which is called The green color has faded, turning yellow .
From the spectrum in Fig.
, it can be predicted that the presence of chlorophyll a that lost a central magnesium atom is called pheophytin a because Fig 2.
The spectrum of C.
xanthorrhiza extract .
pH 1 to 7 and .
pH 8 to 13 Pirim Setiarso et al.
Indones.
Chem.
, 2023, 23 .
, 924 - 936
Fig 3.
The spectrum of A.
cordifolia extract .
pH 1 to 7 and .
pH 8 to 13 chlorophyll a absorbs red light at approximately 662 nm and violet light at approximately 430 nm.
Then the absorption peak appears at 468 nm, which indicates the presence of anthocyanin molecules .
However, the treatment of pH 1Ae7 affects the absorbance.
Where the increase in pH from 1 to 7, the absorbance also increases.
The increase in absorbance is related to the number of molecules or the concentration of chlorophyll a that has been extracted.
Then it can be seen in Fig.
, there is no shift in wavelength at pH 8Ae11.
The absorption pattern is still the same with pH 1Ae7.
However, there was a decrease in absorbance at pH 8Ae11.
This is related to the quantity of molecules or the concentration of chlorophyll a that is extracted less.
At pH 12 there is a change in the wavelength absorption.
The resulting wavelengths are 640 and 412 nm.
Predictably this absorption is an intact chlorophyll b with a central magnesium atom.
At pH 12 there was also no absorption peak at a wavelength of 468 nm, which indicated that anthocyanin compounds were not extracted at this pH.
At pH 13, the resulting wavelengths are 660 and 401 nm.
There is a shift of 664 to 660 nm.
Predictably at the top is the presence of an intact chlorophyll a with magnesium as the central atom.
Besides that, there is a shift in the absorption of the wavelength at the peak of 412 to 401 nm.
This is related to the chlorophyll a which is hydrolyzed into chlorophyllide a and phytol group .
Band Gap Determined of Cyclic Voltammetry The band gap energy of the extraction results with pH Pirim Setiarso et al.
treatment was determined by the CV method.
Measurements were made at a scan rate of 20 mV/s at a potential range of Oe1 to 1 V.
The band gap energy was determined from the difference between HOMO and LUMO values.
If the difference between the HOMO and LUMO values is getting smaller, the better the quality of the extracted dye.
The ability to regenerate dyes shows the ease of electron transfer from electrolyte IOe/I3Oe to the HOMO band of the substance.
This is related to the easier process of excitation of dye electrons from the valence band to the conduction band.
with sufficiently small energy, the electrons can be excited.
The conduction band is affected by the TiO2.
which the effect of TiO2 will be in line with the energy of the LUMO dye compound, the easier it is for electron injection.
The values calculated in the equation below involve 4.
40 eV as the standard energy level of iodine electrolyte below the vacuum level .
Thus, the HOMO.
LUMO, and band gap energy values can be calculated by Eq.
E HOMO A A e A E ox A 4.
40 A eV E LUMO A A e A Ered A 4.
40 A eV E g A E LUMO A E HOMO The HOMO value is correlated with the oxidation state .
xidation pea.
, while the LUMO is correlated with the reduction state .
eduction pea.
of the CV .
The CV can be seen in Fig.
This research will study the combination of dye mixtures and compositions.
The band gap energy values are summarized in Table 1.
the range of pH 1 to 7, the best band gap energy of C.
Indones.
Chem.
, 2023, 23 .
, 924 - 936
xanthorrhiza extract was at pH 1 of 0.
66 eV.
While in the pH range 1 to 7, the best band gap energy is found at pH 7 of 0.
96 V.
The A.
cordifolia extract in the range of pH 8 to 13 has the best band gap energy at pH 13 of 0.
43 eV.
Meanwhile, in the range of pH 8 to 13, the best band gap energy at pH 12 is 0.
65 eV.
Of all the dye extraction results with pH variations that have been described, all of them have the potential to become sensitizers in DSSC.
However, the band gap energy is taken from this optimum pH to be used for mixing variations.
Characterization was also carried out by UV-Vis spectroscopy and The bandgap energy of TiO2 is 3.
2 eV .
The LUMO TiO2 energy has been determined to be Oe4.
00 eV .
So that the excitation of electrons from the dye will be easier to inject into the TiO2 layer when exposed to light.
Therefore, the dye produced in this study has the potential as a DSSC sensitizer and is expected to increase DSSC efficiency.
Electrons are injected into the conduction band of the porous semiconductor layer because the LUMO of the dye has a higher energy level than that of the conduction layer.
Suggesting that the electron injection from these LUMOs to the TiO2 conduction band is possible.
Use of TiO2 for a variety of benefits, including it is stable, can be used as an electrode in photoelectrochemical systems operating at high temperatures, is inexpensive, non-toxic, and has good optical properties that aid the injection of excited dye electrons into the semiconductor .
UV-Vis Spectroscopic Characterization of Mixed Extracts This characterization is viewed from the best band gap energy determined by the previous CV method.
this study, the extract was mixed in two parts, acid and Under acidic conditions, the extracts of pH 7 and 1 were mixed, while in alkaline conditions, the extracts Fig 4.
Cyclic voltammogram of C.
xanthorrhiza extract .
pH 1 to 7 .
pH 8 to 13, and A.
cordifolia extract .
pH 1 to 7, .
pH 8 to 13 Pirim Setiarso et al.
Indones.
Chem.
, 2023, 23 .
, 924 - 936
Table 1.
Energy band gap between HOMO and LUMO, extraction results with variations in pH
xanthorrhiza extract
HOMO
LUMO
Band gap .
V) .
V) .
V) were mixed with pH 12 and 13.
The mixture was varied in the composition ratio of 1:4, 2:3, 1:1, 3:2, and 4:1 (A.
cordifolia extract: C.
xanthorrhiza extrac.
The results of mixing extract pH 7 and 1 with a composition ratio of 1:4, 2:3, 1:1, 3:2, and 4:1 resulted in the final pH being 1.
2, 1.
5, 1.
6, 1.
7, and 2.
UV-Vis spectrum resulting from a mixture of pH 7 and 1 with various composition ratios can be seen in Fig.
The spectrum which is generated from the entire composition mixture shows the dominance of curcumin molecules.
The resulting absorption peak is 423 nm, and for a mixture of 4:1, composition is 422 nm.
Almost no visible signs of the presence of chlorophyll molecules.
This is because the ethanol solvent does show a more suitable level of polarity in the curcumin molecule than in Basically, the curcumin molecule produces a higher concentration when extracted using ethanol than Chlorophyll has a side chain called phytol in which there are many methyl functional groups, thus reducing the polarity when extraction using ethanol If seen, indeed, the curcumin molecule produces a relatively higher absorbance in the previous characterization than chlorophyll.
The results of mixing extract pH 12 and 13 with a composition ratio of 1:4, 2:3, 1:1, 3:2, and 4:1 resulted in the final pH is 12.
6, 12.
4, 12.
3, 12.
2, and 12.
UV-Vis spectrum Pirim Setiarso et al.
cordifolia extract
HOMO
LUMO
Band gap .
V) .
V) .
V) Fig 5.
UV-Vis spectrum mixture composition A.
cordifolia pH 7 and C.
xanthorrhiza pH 1 resulting from a mixture of pH 12 and 13 with various composition ratios can be seen in Fig.
The spectrum which resulted is still the same as before, namely the dominance of curcumin molecules and no signs of the presence of chlorophyll molecules.
A mixture of 1:4 composition resulted in a strong peak at 417 nm and a shoulder peak at 439 nm.
At a mixture of 2:3 and 1:1 composition, it resulted in a strong peak at 417 nm and a broad peak at 438 nm.
Then a mixture of 3:2 composition resulted in an absorption peak at 419 nm, and no shoulder peak appeared as in the previous Indones.
Chem.
, 2023, 23 .
, 924 - 936
Finally, the 4:1 composition mixture only produces an absorption peak at 417 nm, and the shoulder peak that appears is not too strong and sharp.
This shows that the composition mixture only shifts the absorption peak slightly so that it experiences a bathochromic effect on the shoulder peak and a hypochromic effect on the strong peak.
Determination Band Gap of Mixed Extracts This characterization is based on the best band gap energy determined by the previous CV method on each dye that has the best pH for acidic and alkaline conditions.
In acidic conditions.
cordifolia extract with pH 7 and xanthorrhiza extract with pH 1 were combined, while in alkaline conditions.
cordifolia extract with pH 12 was combined with C.
xanthorrhiza extract with pH 13.
Each of these combinations varied with composition ratios of 1:4, 2:3, 1:1, 3:2, and 4:1 (A.
cordifolia extract: C.
xanthorrhiza extrac.
The CV can be seen in Fig.
In a mixture of extracts pH 7 and 1, the best band gap was obtained at a composition of 3:2 with a final pH pH 1.
7 is the most optimal concentration in the extract mixture.
This is because at this pH, it has the lowest band gap among the other mixtures, as shown in Table 2.
The smaller the band gap in the mixture, the easier the dye electron excitation process from the valence band to the conduction band will be, so the quality of the mixed dye will be better.
When exposed to light, the electrons will be excited properly and consequently inject into the TiO2 layer.
Higher concentration could cause an obstacle to the total electron excitation process, so the excitation does not take place optimally.
The results of measurements of HOMO-LUMO energy and energy band gap A.
cordifolia extract mixture .
H .
and C.
xanthorrhiza extract .
H .
as well as a mixture of A.
cordifolia extract .
H .
and C.
xanthorrhiza extract .
H .
were determined by voltammetry can be seen in Tables 2 and 3.
The best bandgap composition in the mixed extract pH 12 and 13, a composition of 1:4, was found with a final pH of 12.
The molecular concentration at pH 12.
is considered the most optimal.
The curcumin molecules extracted at pH 13 were less, therefore the composition Fig 6.
UV-Vis spectrum mixture composition A.
cordifolia pH 12 and C.
xanthorrhiza pH 13 Fig 7.
Cyclic voltammogram mixture composition .
cordifolia pH 7 and C.
xanthorrhiza pH 1 .
pH 12 and C.
xanthorrhiza pH 13 Pirim Setiarso et al.
Indones.
Chem.
, 2023, 23 .
, 924 - 936
Table 2.
HOMO.
LUMO, and band gap mixture pH 7 and 1 Mixture of A.
cordifolia extract .
H .
and C.
xanthorrhiza extract .
H .
HOMO
LUMO
Band gap .
V) .
V) .
V) Mixture pH 1.
pH 1.
pH 1.
pH 1.
pH 2.
Table 3.
HOMO.
LUMO, and band gap mixture pH 12 and pH 13 Mixture pH 12.
pH 12.
pH 12.
pH 12.
pH 12.
Mixture of A.
cordifolia extract .
H .
and C.
xanthorrhiza extract .
H .
HOMO
LUMO
Band gap .
V) .
V) .
V) of the mixture at pH 12.
6 was more abundant than C.
xanthorrhiza extract.
The composition ratio between chlorophyll b and curcumin molecules is optimum in this composition because it has a smaller band gap than C.
xanthorrhiza extract or A.
cordifolia extract.
In a mixture of these compositions, both can excite electrons well when exposed to light.
DSSC Performance Sensitized Selected Compositions of Dyes Mixture DSSC performance was tested using a 10-watt LED lamp with a light intensity of 509.
554 mW/cm2.
The distance between the lamp and the DSSC is 4 cm.
Measurement of DSSC performance using a potentiometer as reported by Setyawati et al.
Characterization includes Voc.
Isc.
Fill Factor, and The summary and characterization of the I-V curve of the DSSC can be seen in Table 4 and Fig.
In this study, a mixture of pH 7 and 1 extracts was selected at a ratio of 3:2 with a pH of 1.
This combination resulted in cell parameters of Isc = 2.
5 A,
Voc = 320 mV, and FF = 1.
83, with a maximum cell efficiency of 0.
Under acidic conditions, curcumin molecules tend to be stable and maintain their structure.
However, in the extraction process, the pH treatment affected the concentration of the extracted curcumin molecules, so the best was chosen .
Meanwhile, chlorophyll in acidic conditions affects the release of a magnesium atom as the central atom of the chlorophyll In addition, the presence of anthocyanins was detected at this pH when extracted.
This is associated with the greater steric hindrance when mixing, which will affect the binding to the TiO2 layer, and also the injection of electrons into the TiO2 layer when exposed to light.
The structure of the anthocyanins may influence DSSC performance.
For example, if the structure includes Table 4.
Characterization DSSC mixture of the best composition A.
cordifolia extract and C.
xanthorrhiza extract Extract mixture .
H) 7 and 1 12 and 13 Pirim Setiarso et al.
Composition ratio 3:2 pH 1.
1:4 pH 12.
Voc
V) Isc
(A)
Efficiency (%) Indones.
Chem.
, 2023, 23 .
, 924 - 936
of this combination has the smallest band gap energy that has been determined by cyclic voltammetry and also characterized using UV-Vis spectroscopy.
The observed cell parameters from this combination were Isc = 3.
3 A,
Voc = 407 mV, and FF = 1.
67, with the maximum cell efficiency obtained being 0.
n Fig 8.
I-V Curves DSSC mixture of the best composition cordifolia extract and C.
xanthorrhiza extract a longer R group, the steric hindrance for the anthocyanin to form a bond with the oxide surface of the TiO2.
As a result, it efficiently blocks the molecule from chemical adsorption on the TiO2 film layer.
Therefore, in this study, the best pH was also selected, and the best mixture composition was also selected to produce optimal efficiency when used as a dye sensitizer in DSSC.
Under alkaline conditions, a mixture of pH 12 and 13 was chosen with a ratio of 1:4 to produce a final pH of 6, to be used as a dye sensitizer in DSSC.
In the alkaline phase, curcumin molecules have hydrolysis so that they are degraded.
This causes a change in the chromophore group, which results in a change in visible light absorption, resulting in a smaller band gap for electron Then chlorophyll at this pH is predicted as pure chlorophyll without anthocyanins, and also, the central magnesium atom cannot be separated.
So that when mixing, the steric resistance that occurs is smaller than that of the acidic phase.
This makes the process of chemical bonding by the dye functional groups to the TiO2 layer easier, and also, when exposed to light, it will be easier to inject electrons into the TiO2 layer.
At this stage, the selection of the best composition is also carried out to obtain optimal efficiency and sensitivity to sunlight.
In alkaline conditions, the best combination of A.
cordifolia extract pH 12 with C.
xanthorrhiza extract pH 13 is a ratio of 1:4 with a final pH of 12.
The composition Pirim Setiarso et al.
CONCLUSION
Sensitized DSSC from extracts of C.
and A.
cordifolia with pH treatment has been successfully fabricated.
The UV-Vis spectrum shows that the extracted pigment contains curcumin and chlorophyll compounds.
The pH treatment also showed a shift in the characteristics of the absorption peak associated with changes in the chromophore and auxochrome groups in the molecule.
The band gap energy of the extracted dye, by pH treatment, was determined using cyclic voltammetry.
These two dyes have the potential to be applied as DSSC sensitizers.
The best mixture of these two dyes (A.
cordifolia extract:C.
xanthorrhiza extrac.
was found at pH 7 and 1 with a composition of 3:2 pH 1.
7, producing Voc.
Isc.
FF, and , of 320 mV, 2.
5 A, 1.
83, and 0.
096%, respectively.
Then at pH 12 and 13 with a composition of 1:4 pH 6, it produced Voc.
Isc.
FF, and , of 407 mV, 3.
3 A,
67, and 0.
146%, respectively.
n AUTHOR CONTRIBUTIONS Rifanda Viantiano Harsono and Pirim Setiarso contributed to the extraction of curcuma rhizome and binahong leaves as well as the fabrication of DSSC.
Nita Kusumawati contributed to the UV-Vis analysis.
addition, this article manuscript was written by all n REFERENCES