International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol 3 .
, 2022 .
https://ijeise.
id/ E-ISSN: 2721-8775 Corrosion Inhibition Effect of the Essential Oil of Dried and Fresh Crystal Seedless Guava Leaves (Psidium guajav.
in Acid Medium Lilik Suprianti1,a*.
Nove Kartika Erliyanti1,b.
Caecilia Pujiastuti1,c Chemical Engineering Department.
University of Pembangunan Nasional AuVeteranAy Jawa Timur Jl.
Raya Rungkut madya.
Gunung Anyar Surabaya, 60294.
Indonesia E-mail: aliliksuprianti.
tk@upnjatim.
id , bnove.
tk@upnjatim.
ccaeciliapujiastuti@gmail.
*Corresponding author: aliliksuprianti.
tk@upnjatim.
Received: 20th September 2021.
Revised: 30th October 2021.
Accepted: 20th April 2022.
Available online: 19th May 2022.
Published regularly: May and November.
Abstract This research studied the corrosion inhibition activities of the essential oil of crystal seedless guava leaves (Psidium guajav.
in an acid medium.
The essential oil (EO) was extracted from the different treatments of raw materials .
resh and dried leave.
using the microwave hydrodistillation method with a power of 600 Watt.
Water was used as the solvent, with the ratio of feed to solvent .
1:7.
The extraction duration was over 3 hours.
The extraction process was done at atmospheric pressure and 100oC.
Different raw material treatments result in different yields, where the highest yield was obtained from the dried leave, with the value reaching 1.
The essential oil chemical compound was determined by GC-MS The main component obtained were caryophyllene .
98%) and Caryophyllene oxide .
96%).
The essential oil was applied as a corrosion inhibitor for carbon steel in a 1 M Hydrochloric acid (HC.
The inhibition efficiency (IE) was 67% at a concentration of 0.
3g/L, while the fresh leaves essential oil was only 63%.
The dried leave EO performs a higher anti-corrosion effect than the fresh leaves EO.
These results show crystal seedless guava leaves' essential oil has anti-corrosion activities on carbon steel in an acid medium.
Keywords: Psidium guajava, essential oil, extraction, microwave hydrodistillation, corrosion inhibitor Introduction Carbon steel is widely used in industry due to its low cost and mechanical strength.
Carbon steel has a high carbon content of about 0.
2Ae2.
65%), copper .
6%), and silicon .
6%).
However, carbon steel is highly reactive and undergoes corrosion when exposed to an acidic environment .
Corrosion is the metal degradation because of the electrochemical reaction between the metal and the environtment.
Corrosion is a spontaneous process that happens naturally.
Many efforts have been made to prevent carbon steel corrosion due to acid environments.
One of them is by adding corrosion inhibitors.
Corrosion DOI: https://doi.
org/10.
33005/ijeise.
inhibitors are compounds that, when added in small concentrations to a corrosive media, decrease or prevent the reaction of the metal with the media .
Important corrosion inhibitors addition applications are acid pickling, industrial acid cleaning, acid descaling, and oil well acidizing .
Most corrosion inhibitors contain toxic components that are dangerous to the environment .
, so organic corrosion inhibitors become interesting to be investigated due to their environmental friendly.
On the other hand, the essential oil is an excellent and eco-friendly inhibitor under diverse corrosive environments and biofilms for most Essential oils are liquids extracted from International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol.
, 2022
plants consisting of volatile aroma compounds.
Some techniques to extract the oil from the plants are distillation, solvent extraction, oil extraction.
Previous research has studied the comparison of some essential oil extraction techniques.
Ranging from convention methods of hydrodistillation (HD), steam distillation (SD), turbohydrodistillation (THD) to innovative techniques, such as ultrasound-assisted extraction (US-SD) and microwave-assisted extraction The result found that the best result was the microwave hydro diffusion and gravity (MHG) method.
The same result was investigated by Moradi et.
They found that the Microwave hydrodistillation was superior in saving energy and extraction time to traditional distillation.
The application of essential oils from many sources as corrosion inhibitors has been Artemisia herba alba has an inhibitor efficiency of 74% when applied on steel in 0.
H2SO4 medium.
Atlas cedar essential oil inhibits the corrosion of steel in 1 M HCl with an efficiency of 88% .
Salvia aucheri mesatlantica showed the inhibitor efficiency 86.
12% for the corrosion of steel in 0.
5 M H2SO4.
Eucalyptus globulus essential oil has been applied for C38 steel 5 M Sulfuric Acid Solution and gave inhibition efficiency 81% .
Application Mentha Spicata essential oil on the Corrosion of Steel in 1 M Hydrochloric Acid found the inhibition efficiency reach 97%.
Essential oil from Psidium guajava's leaves is one potential resource for corrosion inhibitors.
is because crystal guava plants are easy to grow in tropical areas.
Indonesia has many Crystal guava So far, people take advantage only of the fruit, while the crystal guava leaves are only utilized as functional food, such as tea and diarrhea medicine.
Generally, the leaves are discarded and do not utilize optimally.
The composition of oil contained in guava leaves include iso-caryophyllene .
53%),
00%), farnesene .
65%),
84%), decadinene .
75%), acopaene .
80%), a-humulene .
74%), and scadinol .
08%) .
Previous investigations about the potential use of the Crystal guava's leave for corrosion inhibitors have been done by Hartanto et al.
The extraction process was done by using the maceration technique.
The Psidium guajava DOI: https://doi.
org/10.
33005/ijeise.
leaves extract was applied as a corrosion inhibitor for stainless steel in a 3% NaCl medium.
The inhibition efficiency obtained was 37.
93% by inhibitor concentration of 1000 ppm.
Since the chemical composition of Psidium guajava leaves essential oil has potential use as a corrosion inhibitor, this research aims to extract the essential oil of Psidium guajava leaves and study its potential as a corrosion inhibitor for carbon steel in dilute Hydrochloric Acid solution.
Material and Method Material The raw material used in this study was crystal guava leaves obtained from Prambon District.
Sidoarjo.
East Java.
The leaves were taken from the waste of cutting stalk.
The raw material was prepared in two conditions: fresh and dried leaves.
The Fresh leaves are leaves that have just been cut from the tree, while the dried leaves are leaves that have been dried.
The drying process was done using a box dryer at 50 oC for 4 hours.
Crystal seedless guava leaves .
resh and drie.
are then reduced to A 1 cm in size.
Another material used in this experiment is demineralized water as the solvent.
The specimen for corrosion rate analysis was carbon steel with iron and carbon composition.
A specimen was cut at 10y10y3 mm.
One side of this specimen was connected to a copper wire covered with a plastic tube to avoid contact with the environment.
The specimens were polished using emery paper of grades 1000.
Then, specimens were washed with demineralized water and acetone.
An aggressive solution of 1 M HCl was prepared by diluting 98% HCl using demineralized water.
Equipment The main equipment used in this study was a microwave as a heater equipped with a clevengertype apparatus.
The additional equipment parts are a condenser, regulator, and temperature indicator.
The main tools consist of a 100 ml distiller flask and a microwave that has been installed with a power regulator .
he lowest microwave power is 150 Watt and the highest power is 600 Wat.
has a 2450 MHz frequency.
The microwave is equipped with a time controller.
The supporting equipment includes .
Clevenger, .
reflux condenser, .
condenser, .
temperature regulator and indicator, and .
essential oil product The design of this research tool is International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol.
, 2022
adopted from previous research tools conducted by Pujiastuti et al.
, as shown in figure 1 .
before extraction ycoyca .
Secondly, weighted the essential oil that was obtained from the extraction process ycoyca .
Thirdly calculate the yield by using the following equation weight of collected oil dry weight initial leave The Refractive index was measured by using a Calibrate the refractometer by using demineralized water.
The water temperature should be no more than 20oC.
Put the oil in the sample area and wait until the oil temperature is The reading was done by seeing the scale from the eyepiece part of the refractometer The essential oil density has been determined using a 5 ml pycnometer at 25oC.
the density calculate simply using the equation Figure 1 Schematic of the Research Tool for Extracting Essential Oil from Crystal Seedless Guava Leaves Using the Microwave Hydrodistillation Method Research Methods Psidium guajava leave extraction The method in this research is essential oil extraction using the microwave hydrodistillation (MHD) process.
Firstly, weighted 50-gram crystal seedless guava leaves that have been prepared before and put into a flask.
Secondly, add the demineralized water into the flask with a ratio of feed to solvent .
1:7.
The next step is to put the flask into a microwave equipped with a thermocouple and temperature control.
Turn on the microwave to start the extraction process for 3 hours.
The operating condition was set at atmospheric pressure and temperature of A 100 oC, with a microwave power of 600 Watt.
A condenser was used to condense the vapour phase into a liquid phase.
At the same time, clavenger recycled water condensates into the distillation flask to keep the ratio of the material to the solvent.
It prevents the distillation flask run out of solvent.
After 3 hours, the distillate was taken and separated between the solvent and the extracted oil.
The oil is then stored in sealed glass vials at 4oC for later analysis.
This method was based on the best condition from the previous study by Erliyanti et al.
Physical properties Analysis The essential oils have been analyzed in the yield, density and refractive index.
To determine the yield, firstly weighed the Psidium guajava leave DOI: https://doi.
org/10.
33005/ijeise.
yuU= ycoycyycnycaycuycu ycuycnyco Oe ycoycyycnycaycuycu ycOycyycnycaycuycu Where, yco = ycoycaycyc .
, ycO = ycycuycoycycoyce .
Chemical properties Analysis GC-MS analysis was carried out in an ISQ 7000 mass spectrometer (Thermo Scientific.
USA) with AEI .
dvance electron ionizatio.
The samples were prepared by dissolving 50 L in a 1 mL final volume of methanol, then injected 1 L of solution into a column (TG-SQC GC, 15 m 25 mm x 0.
with AS 1310 autosampler injection system (Thermo Scientific.
USA).
Helium gas was used as the carrier at a 1 mL/min constant flow rate.
The injector temperature and MS transfer line temperature were 200 oC.
The GC-MS analysys was taken at Instrument laboratory.
University of Pembangunan Nasional Veteran jawa Timur.
Electrochemical Measurement Electrochemical measurement was used to determine the corrosion rate of the steel before and after adding the inhibitor.
The electrochemical measurements were carried out using a three-electrode setup comprised of an electrode .
raphite ro.
, a working electrode .
arbon stee.
, and a reference electrode .
aturated calomel electrod.
The Working electrode .
arbon stell specime.
surface area was prepared as described in the material and method section.
International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol.
, 2022
The sample surface area was covered by resin on the backside.
Then, it was dipped in the corrosion solution.
The scan rate was applied at 1mV/s for testing polarization.
The time limit for reaching equilibrium potential before the electrochemical measurement was 30 minutes.
Results and Discussion 1 Physical Properties Study The current investigation extracted essential oil from Psidium Guajava leaves from fresh and dried leaves.
The microwave hydrodistillation process was chosen to extract the essential oil from Psidium guajava leaves for high-yield The microwave power was set at 600 watts, and the extraction duration was three hours.
The ratio of raw material to the solvent was 1:7 .
The essential oil extract from both fresh and dried Psidium guajava leaves was determined by their physical properties, such as density and refractive indexAithe result is shown in table 1.
The higher the molecular weight of the essential oil, the higher the density .
The raw material condition did not significantly influence the refractive index of the extracted essential oil.
The refractive index of the essential oil is in the range of 1,8-1,5.
From our research, the best yield, the density and the refractive index value obtained during the extraction process of the dried seedless guava, i.
1,085, 0.
949 gr/ml, and 1.
498, respectively.
2 Chemical Study The effect of the Psidium guajava leaves raw material condition before extraction to the chemical compound of the essential oil Gas Chromatography-Mass Spectroscop.
GC-MS analysis.
The chemical compound analysis was done by MS quantitative The raw material condition, both the fresh and dried leaves, are presented in table 2.
Table 2 Chemical composition of fresh and dried crystal seedless guava leaves essential oils Table 1 The physical properties of essential oil from fresh and dried Psidium guajava leaves Treatment
of leaves Yield
(%)
Density .
ram/m.
Refractive Fresh Dried Data in table 1 show that the different raw material conditions significantly differ the yield.
The dried leaves resulted in a higher yield than the fresh leaves.
The drying process of the raw materials helped the essential oil gland open easily because of the heat from the oven.
It made the essential oil extracted more rapidly than the fresh leaves .
The power of the microwave of 600 watts helped the extraction process effectively.
The high power of microwave increases the extraction temperature and increases the evaporation rate, so the essenteial oil's solvent evaporates and separates from the oil.
The microwave's high power also transfers the high energy to the material and converts it to the high temperatur, resulting in a higher yield of the essential oil.
The less solvent in the essential oil from the Psidium guajava leaves increases the oil's The product was also denser and more The higher the evaporation rate, the essential the oil component to be extracted and the higher the molecular weight of the essential oil.
The essential oil molecular weight influences their DOI: https://doi.
org/10.
33005/ijeise.
Essential oil `(%) Fresh Dried Copaene Caryophyllene Caryophyllene oxide Caryophylla4.
,8.
-dien-5a-ol Aromandrendene Isoaromadendrene Humulene Tumerone 1,3,6,10Dodecatetraene, 3,7,11-trimethyl-, (Z,E) (-)-Globulol Table 2 shows that the raw material condition influenced the chemical compound of the essential oil.
The dried leaves resulted in the caryophyllene more than the fresh leaves.
Caryophyllene is the essential oil compound in the essential oil from Psidium guajava leaves.
The dried leaves contain 44,98% Caryophyllene, higher than that contained in the essential oil from the fresh The highest Caryophyllene compound resulted from the extraction of the dried Psidium Guajava leaves at the power of 600 watts, and the International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol.
, 2022
ratio of the leaves to the solvent is 1:7 .
it has a good agreement with the previous research that was done by Weli et al.
in 2019, where the extraction of the essential oil from Psidium guajava leaves with the conventional method resulted in the essential oil with the compound of Caryophyllene 33,53% .
Iycaycuycyc the corrosion current density in the absence of an inhibitor.
The value of corrosion potential (Ecor.
, cathodic Tafel slope .
, anodic Tafel slope .
Corrosion Table 3 Electrochemical parameters and the corresponding corrosion inhibition efficiencies for the corrosion of carbon steel in 1 M HCl containing psidium guajava leave essential oil 3 Electrochemical Study The efficiency of the guava leaves essential oil as a corrosion inhibitor was evaluated by the polarization curve technique.
The anodic and cathodic polarization curve of the carbon steel electrode in an acid medium with the presence of different raw material treatments .
resh leave and dried leav.
at 25oC was shown in Fig.
Figure 2 polarization plots of carbon steel in 1M HCl in absence and presence the esential oil from different raw material treatment .
resh and dried psidium guajava leav.
The polarization curves are extrapolated to find the intersection point between potential anodic and potential cathodic.
From the intersection curve resulting ordinate corrosion current.
Icorr, corrosion potential.
Ecorr.
Tafel constant anodic .
cayca ) and Tafel's constant cathodic .
cayca ).
The anodic constant .
cayca ) value is attributed to metal dissolution and adsorption of the inhibitor at anodic potentials, whereas the cathodic constant .
cayca ) is related to hydrogen evolution at cathodic potentials .
Icorr data were used to calculate the inhibition efficiency (IE) by using the following yaycu Oeya yaya (%) = ycaycuycyc0 ycaycuycyc ycu100 where Icorr is the corrosion current at a particular essential oil concentration in the solution, and DOI: https://doi.
org/10.
33005/ijeise.
-Ecorr .
V) .
V) (A/cm Blank 094 x10-5 Dried Fresh 007 x10-5 105 x10-5 .
(%) Rate (CR) and inhibition efficiency (IE(%)) are shown in Table 3.
From the result shown in Table 3, we can deduce that after adding the essential oil to the 1 M HCl solution, the carbon steel electrode was inhibited both in cathodic and anodic.
It is seen in the decrease of the corrosion rate from 0.
359 mm/y 117 mm/y for dried leave EO and 0.
mm/y for fresh leave EO.
The EO protected the carbon steel from corrosion by adsorption its chemical constituent on the carbon steel surface .
The presence of essential oil in the solution reduces the hydrogen ion at the cathode and the dissolution reaction at the anode .
arbon stee.
The EO from dried leave also showed a slightly more efficient than the fresh leave EO.
may seem because of the different physical properties, where the dried leave EO has a higher density than the fresh leave EO.
This result also showed that the Psidium guajava essential oil has a higher inhibitory effect than their extract, which was only 37.
Conclusions This research concluded that the treatment of raw materials Psidium guajava leaves significantly affects the yield and density of essential oils but did not significantly affect the refractive index.
The dried leaves showed better physical properties performance than the fresh leave.
The essential oils obtained from both raw material treatments can be applied as a corrosion inhibitor for carbon steel in an HCl 1 M medium.
The inhibition International Journal of Eco-Innovation in Science and Engineering (IJEISE) Vol.
, 2022
efficiency for dried leave EO and fresh leave EO is 67% and 64%, respectively.
Acknowledgement The researcher would like to thank the LPPM.
University of Pembangunan Nasional AuVeteranAy Jawa Timur for its financial support through Riset Dasar Lanjutan.