Jurnal Akademika Kimia, 11.
: 72-76.
May 2022 ISSN .
2477-5185 | ISSN .
2302-6030 http://jurnal.
id/index.
php/jak/ OPEN ACCESS Characterization of Natural Clay from Gowa Regency.
South Sulawesi Province.
Indonesia Sumiati Side & Suriati E.
Putri* Department of Chemistry.
Faculty of Mathematics and Natural Sciences-Universitas Negeri Makassar-Indonesia 90224 Received 06 March 2022.
Revised 01 April 2022.
Accepted 04 May 2022 doi: 10.
22487/j24775185.
Abstract Clay is one of the essential natural minerals in human life, especially in the industrial sector, which is widely used as a raw material for ceramics fabrication, adsorbents, and photocatalysts.
The characteristics of clay significantly affect the quality of the resulting material.
This study will study the aspects of natural clay in Gowa Regency.
South Sulawesi Province, without the leaching process and with acid leaching.
Acid leaching uses 3 M HCl, previously roasted at a temperature of 600 oC.
The characterization consisted of metal oxide analysis using XRF, mineral content analysis using XRD, morphological analysis, and compound content using SEM-EDX.
The results showed that the primary metal oxide content in natural clay was Fe2O3.
Al2O3, and SiO2, the content of Fe2O3 decreased after the raw clay was treated with acid.
The main mineral content in the sample is quartz, kaolinite, and hematite.
The sample's morphology looks different after being given acid treatment.
the acid leaching natural clay sample shows a porous morphology, while the natural clay without acid leaching shows the morphology in the form of lumps.
The EDX mapping analysis showed that the number of impurities decreased after being given acid treatment.
Keywords: Natural clay, mineral content, morphology, acid leaching an adsorbent, and as a photocatalyst (Khennaoui et , 2.
One of the essential things that must be studied before using clay in this application is the mineral content, metal oxides, and characteristics of natural clay.
The mineralogy of clay constituents significantly affects the expansive properties of clay (Utami, 2.
Based on the results before.
Kagonby et al.
studied the mineral content of Cameroon's natural clay minerals, containing smectites, illite, kaolinite, quartz, feldspar, and mica.
The metal oxide content consists of SiO2 .
-55%).
Al2O3 .
1%), and Fe2O3 .
82%).
The same study was done by Tsozuy et al.
, who studied the mineral content and physicochemical natural clay from Maroua Cameroon and reported that the mineral content contained is quartz and feldspar, and plagioclase.
the dominant metal oxide content is SiO2.
Al2O3, and Fe2O3.
Putri & Pratiwi .
also reported high content of silica .
39%) and alumina .
02%), as well as some impurities, contained such as Fe2O3 and TiO2.
Several methods have been used to remove impurities in clay minerals, including acid leaching (Tripathy et al.
, 2.
, alkaline leaching (Li et al.
, high pressure (Wu et al.
, 2.
, and high temperature (Bai et al.
, 2.
High pressure and high-temperature methods also use acid or base Introduction Indonesia is a country that has abundant natural resource potential.
One of them is natural Among natural minerals, metal oxides are the main content with great potential to be developed as the basis for manufacturing advanced and high-tech materials such as alumina (Al2O.
and silica (SiO.
The most important content of alumina and silica metal oxides is in clay, resulting from chemical weathering (Manjate et al.
, 2.
Clay is a layered silicate mineral .
that is plasticity and hardens when heated or dry.
The basic crystal structure of clay minerals consists of one or two layers of silicon dioxide with one sheet of aluminum oxide.
In the silica layer, the basic unit is the silica tetrahedron.
one silica atom is bonded to four oxygen atoms.
If each tetrahedron shares 3 of the other 4 oxygens, it will form a hexagonal structure called a tetrahedral layer.
The basic units of alumina are the octahedron and the hydroxide ion.
Aluminum atoms are bonded to 6 oxygen atoms, and each octahedron atom shares its 6 oxygen atoms to form a hexagonal structure called an octahedral layer.
Clay is one of the essential minerals because it is used as a primary material in various industries, such as in ceramic fabrication (Putri et al.
, 2.
, as a *Correspondence:
Suriati Eka Putri e-mail: ekaputri_chem@unm.
A 2022 the Author.
retain the copyright of this article.
This article is published under the terms of the Creative Commons Attribution-NonCommercial-ShareAlike 4.
0 International, which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.
Volume, 11.
No.
2, 2022, 72-76
Jurnal Akademika Kimia solutions and some additive compounds.
In this study, acid leaching was used to remove impurities contained in natural clay.
Furthermore, it will investigate the characteristics of natural clay obtained from the Gowa Regency.
South Sulawesi.
Indonesia.
The clay studied consisted of natural clay without treatment and natural clay with acid leaching treatment.
Fe2O3 in this clay is similar to the sample used in the previous study (Yadav & Bhattacharyya, 2.
, which uses clay in the form of kaolin and has a relatively high content of Fe2O3 and TiO2.
The high content of Fe2O3 and TiO2 in natural clay is supported by data from mineral analysis using XRD .
hich will be discussed in the next sessio.
The amount of Fe2O3 decreased after the natural clay was acid leached, from 55.
13% to It is because the acid leaching treatment aims to reduce the number of impurities in the raw clay (Chen et al.
, 2.
With the addition of HCl, it is assumed that iron ions will dissolve in acidic solvents to form FeCl3.
Methods Sample preparation The natural clay was dried first, then pulverized and sieved 60 mesh.
the sample used was clay that passed the sieve.
Analysis of mineral content using XRD The mineral content in natural clay was analyzed using XRD.
The analysis is shown in Figure 1.
Acid leaching of natural clay Before leaching the natural clay sample, it was roasted at a temperature of 600 oC in a furnace using a rate of 10 oC/min and a hold time of 2 h.
The leaching process was carried out using 3 M HCl, stirring for 5 hours at 80 oC, then filtered and calcined with calcination temperatures of 900 oC.
Sample characterization The metal oxide content of natural clay samples was analyzed using XRF Thermo Fischer Scientific with vacuum X-Ray path, eff.
0 mm, and eff.
area of 132.
7 mm2.
X-ray diffraction (XRD) was performed using Rigaku Miniflex II with CuK radiation ( = 1.
5405 yI) ranging from 15o O 2 O 80o, and operation at 30 kV and 10 mA.
Scanning electron microscopy (SEM) was performed using a JCM-600Plus scanning electron microscope where the electron beam was set to 15 kV.
Results and Discussion Analysis of metal oxide using XRF The metal oxide content of natural clay before and after acid treatment was analyzed using XRF.
the results obtained are shown in Table 1.
Table 1.
The metal oxide content on natural clay
Composition Fe2O3
SiO2
Al2O3
TiO2
K2O
MnO
CaO
ZrO2
Cr2O3
CuO
SrO
ZnO
Nb2O5
Rb2O
Y2O3
Content .
Natural clay Acid leaching natural clay Figure 1.
Diffractogram natural clay and acid leaching clay Based on Figure 1, it can be seen that the primary minerals contained in the sample are quartz (SiO.
, kaolinite (Al2O3A2SiO2A2H2O), and hematite (Fe2O3.
H2O).
Some minerals with not-sohigh peaks that are thought to act as impurities are goethite (FeOOH), magnetite (Fe3O.
, and anatase (TiO.
This impurity is almost similar to natural clay from Queensland.
Australia, where the impurity minerals in the sample consist of minerals derived from metal oxides of iron and titanium (Pepper et al.
, 2.
The peaks of hematite, goethite, and magnetite in the acid leaching clay sample are not too sharp, so it can be concluded that the impurities in the acid leaching clay sample have decreased after receiving Based on Table 1, the main content in natural clay is Fe2O3,ASiO2, and Al2O3.
The high content of Sumiati Side & Suriati E.
Putri clay samples with an acid treatment and without acid treatment.
The acid-treated samples showed a porous morphology, while the non-acid-treated samples showed a generally dense texture, a unique characteristic of clay minerals.
The appearance of pores in the acid-leaching clay sample indicates the dissolution of some impurities so that the pores on the sample's surface are open.
It is in line with the results of Xu et al.
, which show the morphological changes in clay samples after treatment.
acid treatment.
In addition, the peaks in the acid leaching clay sample were sharper, so this sample was more crystalline than the sample without acid It is in line with the research results of Ferdowsi et al.
, which show a narrowing of the band and a decrease in peak intensity on the diffractogram, indicating a reduction in the number of impurities in the sample.
Analysis morphology using SEM The morphology of the samples was analyzed using SEM, shown in Figure 2.
It can be seen that there are differences in the morphology of natural Figure 2.
Samples morphology using SEM 5 kV with magnification 1000y .
natural clay .
acid leaching clay sample surface.
The results of EDX and mapping analysis are shown in Figure 3.
EDX and mapping analysis EDX and mapping analysis was carried out to determine the elemental content in the sample and the pattern of distribution of elements on the Figure 3.
EDS mapping analysis of .
natural clay and .
acid leaching natural clay Volume, 11.
No.
2, 2022, 72-76
Jurnal Akademika Kimia this is presumably because, at the time of analysis using EDX only specific points (Foroutan et al.
, 2.
Based on Table 2, it is shown that the amount of Fe impurities decreased after being given acid At the same time, the amount of alumina-silica increased after being given acid It happens because the composition of impurities has decreased so that quantitatively the number of alumina-silica increases.
EDX analysis shows that clay minerals are rich in Fe.
Al, and Si.
The most significant element in the sample is oxygen.
The elements of aluminum and silicon are evenly distributed on the sample's The impurity that is quite visible on the surface is elemental iron.
The results of the interpretation of the EDX analysis in the form of mass, atomic, and mole percentages are shown in Table 2.
The number of percentages shown from the results of the EDX analysis is different from the results of the XRF Table 2.
The percentage of the mass, atom, and mol of natural clay and acid leaching clay, corresponding to EDX analysis Mass (%) of element
Element
Compound
Al K
Si K
Fe K
Sr L
Ba L
Tl M
B2O3
Al2O3
SiO2
Fe2O3
SrO
Y2O3
BaO Tl2O3 Atom (%) Natural clay Acid leaching natural clay Natural clay Acid natural clay Mol (%) of compounds Acid Natural clay natural clay concentrated sulfuric acid and alumina extraction process based on it.
Fuel Processing Technology, 92.
, 1213Ae1219.
Chen.
Zhang.
Liu.
Chi.
Chen.
& Chi.
Swelling of clay minerals during the leaching process of weathered crust elution-deposited rare earth ores by magnesium Powder Technology, 367(Ma.
, 889Ae900.
Ferdowsi.
Salem.
, & Salem.
Spectrophotometrical analysis for fabrication of pH-independent nano-sized -alumina by dealumination of kaolin and precipitation in the presence of surfactant composites.
Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, 218(Jul.
, 109Ae118.
Foroutan.
Mohammadi.
Adeleye.
Farjadfard.
Esvandi.
Arfaeinia.
Sorial.
Ramavandi.
, & Sahebi.
Efficient arsenic(V) removal from contaminated water using natural clay and clay composite adsorbents.
Environmental Science and Pollution Research, 26(Octobe.
, 29748Ae Kagonby.
Tsozuy.
Nzeukou.
, &
Ngos.
Mineralogical, physicochemical and ceramic properties of clay materials from Sekandy and Gashiga (North.
Cameroo.
and their suitability in earthenware Heliyon, 7.
, 1-10.
Khennaoui.
Zehani.
Malouki.
Menacer.
, & Lypez.
Chemical Conclusions The results showed that the primary metal oxide content in natural clay was Fe2O3.
Al2O3, and SiO2, the content of Fe2O3 decreased after the raw clay was given acid treatment, from 55.
13% to 83% .
he result of XRF analysi.
The main mineral content in the sample is quartz, kaolinite, and hematite.
The morphology of the samples appeared different after being given acid treatment.
The acid-treated samples showed a porous morphology while the non-acid-treated samples showed a generally dense texture, a unique characteristic of clay minerals.
The EDX mapping analysis showed that the number of impurities decreased after being given acid treatment.
Conflict of Interest The authors declare that we have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Acknowledgment The author's gratitude goes to Lembaga
Penelitian dan Pengabdian Masyarakat (LP2M) Universitas Negeri Makassar for PNBP 2022
funding provided so that this research can be carried References